Severina Iskrač (Avtor), Simona Strnad (Avtor), Suzana Jus (Avtor), Karin Stana-Kleinschek (Avtor), Majda Sfiligoj-Smole (Avtor), Bojana Vončina (Avtor), Mojca Poberžnik (Avtor)

Povzetek

Prispevek obravnava rezultate optimiranja zamreženja tkanin iz močno vite viskozne preje z brezformaldehidnim reagentom. Proučevali smo vpliv koncentracije brezformaldehidnega reagenta za zamreženje, katalizatorja in neionogenega sredstva za mehčanje na nekatere uporabne lastnosti apretirane viskozne preje. Spremljali smo naslednje veličine: stopnjo nabrekanja viskoznih vlaken, barve razlike, pretržno silo, pretržni raztezek in kot razgubanja. Z uporabo brezformaldehidnega reagenta za zamreženje smo dosegli znižanje stopnje nabrekanja viskoznih vlaken za 51,1 do 92,4 %, povečanje kota razgubanja za 60 do 145%, zmanjšanje pretržne sile za 49% do 65% in pretržnega raztezka za 31,6 do 37,6%. Postopek zamreženja ne povzroča zaznavnik barvnih razlik in obarvanih tkanin.

Ključne besede

celulozna vlakna;vrhunsko plemenitenje;brezformaldehidno zamreženje;matematično-statistične metode načrtovanja poskusov;kot razgubanja;mehanske lastnosti;barvna metrika;nabrekljivost viskoznih vlaken;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 677.027.6:677.463
COBISS: 9362966 Povezava se bo odprla v novem oknu
ISSN: 0351-3386
Matična publikacija: Tekstilec
Št. ogledov: 937
Št. prenosov: 77
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Statistical desgning of finishing process for viscose fabrics made from hard twisted yarn - Part 1: Finishing with non-fomaldehyde reagents
Sekundarni povzetek: The paper presents the results of optimizing cross-linking of fabrics made from highly twisted viscose yarn by using the nonformaldehyde reagents. The influence of the crosslinking reagent concentration, catalyst and nonionogenic softener on some applicability properties of the finished viscose fabric was investigated. The following parameters were monitored: the degree of swelling of viscose fibres, elongation at break and crease recovery angle, as well as the influence of the finishing process on the colour of viscose fabrics made from highly twisted yarn. By using the cross-linking non-formaldehyde reagent the degree of swelling of viscose fibres decreased by 51.1 - 92.4%, the crease recovery angle increased by 65 - 145%, the breaking force decreased by 49 - 65%, and the elongation at break decreased by 31.6 - 37.6 %. The crosslinking process did not cause any noticeable colour deviations on the dyed fabric.
Sekundarne ključne besede: cellulose fibers;high-grade finishing;cross-linking with non-formaldehyde reagent;mathematical-statistical methods of experiment designing;angle of decrease;mechanical properties;colorimetry;swelling capacity of viscose fibers;
URN: URN:SI:UM:
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 292-300