Magistrska naloga obravnavan vpliv peskanje na zniževanje zaostalih napetosti v soležnih zvarnih spojih. Za izvedbo te raziskave je bilo narejenih šest preizkušancev iz osnovnega materiala NIOMOL 490 K in eden iz navadnega konstrukcijskega jekla S235JR. Preizkušanci so bili varjeni z različnimi varilnimi postopki T.I.M.E., EPP in MAG. Predhodno so bila izdelana tri obravnavana stanja z različnimi načini zniževanja zaostalih napetosti, kot so: T.I.M.E. 1 varjeno stanje, T.I.M.E. 2 napetostno žarjeno stanje, T.I.M.E.3 vibrirano, EPP 1 varjeno stanje, EPP 2 napetostno žarjeno, EPP 3 vibrirano stanje med varjenjem in MAG varjeno stanje. Vsi preizkušanci razen MAG preizkušanca v varjenem stanju so bili peskani. Meritve zaostalih napetosti po peskanju so bile opravljene z magnetno metodo in primerjane z rezultati, ki so bili pridobljeni pred peskanjem z magnetno metodo. Ugotovljeno je bilo, da se z vnosom tlačnim napetosti s peskanjem zaostale napetosti res znižajo na merilnem mestu na sredini plošče na sredini zvara (x = 0 mm, y = 0 mm).

Ključne besede

zvarni spoji;varjenje;peskanje;merjenje zaostalih napetosti;magnetna metoda;magistrske naloge;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: [U. Videnšek]
UDK: 620.179.14:621.791.053.023(043.2)
COBISS: 22166806 Povezava se bo odprla v novem oknu
Št. ogledov: 883
Št. prenosov: 91
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Influence of shoot peening on residual stress relaxation in butt welded joints
Sekundarni povzetek: In the master's we discussed the influence of shoot peening on residual stress relaxation on butt weld joints. Six samples for the research were made from material NIOMOL 490 K and one was made from construction steel S235JR. Specimens were welded with different welding process such as T.I.M.E., EPP and MAG. Specimens were observed in three different conditions such as EPP 1 as welded, EPP 2 heat treated, EPP 3 vibrated during welding, T.I.M.E.1 as welded, T.I.M.E. 2 heat treated, T.I.M.E. 3 vibrated during welding and MAG as welded. All the specimens were shoot peened expect from MAG as welded specimen. We measured residual stress before and after shoot peening with magnetic method. Then we compered the results and found out that magnitude of the residual compressive stress produced by shoot peening reduced residual stress on the measuring spot in the middle of the butt welded joint (x = 0 mm, y = 0 mm).
Sekundarne ključne besede: weld joints;welding;shoot peening;measuring residual stresses;magnetic method;
URN: URN:SI:UM:
Vrsta dela (COBISS): Magistrsko delo/naloga
Komentar na gradivo: Univ. v Mariboru, Fak. za strojništvo, Konstrukterstvo
Strani: XIII, 51 str.
ID: 10909919