Ultravijolična (UV) svetloba negativno vpliva na obstojnost lesa. Posledično je za boljšo obstojnost treba les zaščititi. Na lignin, sestavino, ki najbolj vpliva na barvo lesa, fotodegradacijski učinki vplivajo najbolj. Za zaščito lesa pred UV-svetlobo uporabljamo tudi nanodelce titanovega dioksida. V raziskavi smo izvedli depozicijo titanovega dioksida na smrekov les in termično modificiran smrekov les. Prisotnost delcev TiO2 na površini lesa smo potrdili z analizo z vrstičnim elektronskim mikroskopom (SEM). Preskušance smo nato premazali s komercialnim pripravkom na osnovi naravnih olj, namenjenim zaščiti lesa na prostem. Vzorce smo izpostavili UV-svetlobi in merili barvo in sijaj. V času 14-dnevnega merjenja smo ugotovili, da se je kot barvno najbolj stabilen izkazal termično modificiran les z depoziti titanovega dioksida ter les, ki je bil premazan z oljem, najslabše pa navaden smrekov les, brez depozitov in olja. Delci titanovega dioksida na termično modificiranem smrekovem lesu izboljšajo odpornost proti UV-svetlobi, medtem ko omenjeni nanodelci v kombinaciji z oljem na navadnem smrekovem lesu ne pokažejo učinka zaščite. Kontaktni kot vode je večji pri preskušancih z oljem. Navzem vode se z zaščito s titanovim dioksidom in oljem zmanjša.

Ključne besede

zaščita lesa;UV-svetloba;titanov dioksid;sprememba barve;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [J. Križan]
UDK: 630*84
COBISS: 2803337 Povezava se bo odprla v novem oknu
Št. ogledov: 1124
Št. prenosov: 299
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Protection of wood against UV-light with titanium dioxide and coatings
Sekundarni povzetek: Ultraviolet (UV) light has a negative influence on durability of wood. In order to increase durability of wood, it should be protected. Lignin, that is the component of wood with the most important influence on its colour, is highly susceptible to photo degradation. Wood can be protected against UV-light also Norway spruce wood and on thermally modified Norway spruce wood was performed. The presence of TiO2 particles on wood was confirmed with the SEM analysis. The specimens were subsequently coated with a commercial oil-based product for protection of wood in exterior. The samples were exposed to UV-light and colour and gloss were measured. During 14-day long exposure it was found, that in terms of colour changes the most stable was thermally modified Norway spruce wood with the deposits of TiO2, and wood with a surface film of the cured oil. The worst colour stability was exhibited by non-modified Norway spruce wood. The results showed that particles of titanium dioxide on thermally modified spruce wood increase its resistance against UV-light, while the TiO2 particles in a combination with the oil did not provide protection against UV-light. Contact angles of water were higher on the specimens with oiled surfaces. Up take of water into wood is decreased by protection with titanium dioxide and oil.
Sekundarne ključne besede: wood protection;UV-light;titanium dioxide;color change;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Komentar na gradivo: Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: VIII, 29 f., [4] f. pril.
ID: 10910300