zaključna naloga Projektno aplikativnega programa I. stopnje Strojništvo
Jakob Štepec (Avtor), Damjan Klobčar (Mentor), Drago Bračun (Komentor)

Povzetek

Konstrukcijsko jeklo predstavlja enega izmed najpogosteje uporabljenih materialov na področju strojništva. Zaradi vse večje geometrijske zapletenosti izdelkov, ki jih ne moremo izdelati z konvecionalnimi tehnologijami so se v zadnjih letih razvile aditivne tehnologije. Uporaba aditivnih tehnologij omogoča izdelavo takšnih izdelkov. Naloga je osredotočena na raziskavo oblikovnega obločnega navarjanja konstrukcijskega jekla. Preizkusi so izvedeni z uporabo CNC stroja in sinergijskega vira toka. Vzorci so izdelani s postopkom varjenja MIG/MAG (angl. Metal active gas / Metal inert gas) in s programom varjenja za manjše brizganje (angl. low spatter) ob uporabi varilne ţice G3Si1 premera 1,2 mm. V okviru diplomske naloge smo preučili vpliv procesnih parametrov, ki omogočajo izdelavo kakovostnih sten. Rezultati naloge kaţejo, da je ob uporabi ustreznih varilnih parametrov in medvarkovne temperature mogoče izdelati stene s širino do 9,11 mm ob izkoristku materiala nad 90 %. Ob izdelavi tako širokih sten lahko te naknadno obdelamo in izdelamo tankostenske izdelke visoke natančnosti.

Ključne besede

diplomske naloge;konstrukcijska jekla;varjenje;navarjanje;aditivne tehnologije;obločno navarjanje žico (WAAM);3D tiskanje;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [J. Štepec]
UDK: 621.791.75:669.14(043.2)
COBISS: 16406811 Povezava se bo odprla v novem oknu
Št. ogledov: 896
Št. prenosov: 442
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Wire and arc additve manufacturing of structural steel
Sekundarni povzetek: Structural steel is among the most widely used material in mechanical engineering. Due to the increasing geometric complexity of products, which precludes the use of conventional technologies, recent years have seen the development of additive manufacturing technologies that make the manufacture of such products practical. This thesis focuses on the research of shape-deposition wire-arc additive manufacturing using structural steel. The experiments were carried out using a CNC machine and a synergic power source. The samples were manufactured by a MIG/MAG welding process using a low spatter welding programme and G3Si1 welding wire of 1.2 mm diameter. Within the scope of this diploma thesis, we researched the effects of process parameters that facilitate the manufacture of quality walls. The results show that choosing appropriate welding parameters and interpass temperatures allows fabrication of walls of up to 9.11 mm thickness with a material utilisation rate of over 90 %. Walls manufactured in this thickness can be subsequently processed to yield thin-walled products of highly accurate shape.
Sekundarne ključne besede: structural steel;welding;metal additive manufacturing;additive technologies;wire - arc additive manufacturing (WAAM);3D printing;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XXII, 50 str.
ID: 10958864
Priporočena dela:
, zaključna naloga Projektno aplikativnega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, ni podatka o podnaslovu
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo