Povzetek

Samocelitveni materiali so sintetično pridobljeni materiali, ki so zmožni popraviti deformacije in ohraniti funkcionalnost po degradaciji ali poškodbi.Taki materiali se dandanes uporabljajo že na mnogih področjih npr. gradbeništvu, avtomobilski industriji, vesoljski tehnologiji,... Dejstvo je, da se takim materialom skozi njihovo uporabo spreminjajo mehanske lastnosti, kar ima lahko velik vpliv na življensko dobo izdelka. V ta namen smo v tej zaključni nalogi ugotavljali, kako se spreminjajo površinske mehanske lastnosti samozacelitvenih materialov glede na število ciklov celjenja.Poleg tega smo proučevali tudi spremembe površinskih mehanskih lastnosti tudi glede na vsebnost komponent, iz katerih je posamezni matterial narejen, saj ima to lahko pomemben vpliv na odločanje ali je nek material uporaben za določen izdelek ali ne. Devetim vzorcem smo v treh ciklih določili površinski modul elastičnosti in trdoto. Cikel je bil sestavljen iz nanoindentacijskih meritev ter analize dobljenih podatkov, mikroskopiranja in zajemanja optičnih slik ter gretja v peči. Rezultati so pri večini vzorcev pokazali, da se s številom ciklov modul elastičnosti zmanjša, trdota pa povečuje. Izkazalo se je tudi, da je sprememba modula elastičnosti največja pri vzorcih z manjšo vsebnostjo Diels-Alderjevih kompoent, sprememba trdote pa pri tistih z večjo vsebnostjo Diels-Alderjevih komponent.

Ključne besede

diplomske naloge;samocelitveni material;nanoindentacija;modul elastičnosti;trdota;površina;Diels-Alderjeva reakcija;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [A. Žibrik]
UDK: 620.178(043.2)
COBISS: 16418075 Povezava se bo odprla v novem oknu
Št. ogledov: 1260
Št. prenosov: 332
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Influence of the healing process on the surface mechanical properties of self-healing materials
Sekundarni povzetek: Self-healing mterials are synthetically created substances that have the ability to repair themselves and recover functionality after degradation, damage and failure. Today, these materials are used in many fields such as civil engineering, automotive industry, aviation,... However, it is also well known, that through their application, they are experiencing changes in mechanical properties, which have a huge impact on the life-time of the product. In the present work were investigating, how the surface mechanical properties of these materials are changing with the healing cycles. Moreover, the influence of the component of which these materials are made of, was studied too. We were measuring elastic modulus and hardness of nine samples, through three cycles of healing process. One cycle included nanoindentation measurement and data analysis, microscopy and optical imaging and heating. The result shown a decrease of elastic modulus and increase of hardness over the cycles of healing. Moreover, the change of elastic modulus was higher for the samples with less DielsAlder components, while the changes in hardness were higher for the samples with higher amount of Diels-Alder components.
Sekundarne ključne besede: Self-healing material;nanoindentation;elastic modulus;hardness;surface;Diels-Alder reaction;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, 31 f.
ID: 10959168
Priporočena dela:
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, diplomsko delo visokošolskega študijskega programa