zaključna naloga univerzitetnega študijskega programa I. stopnje Strojništvo
Anže Smolej (Avtor), Uroš Trdan (Mentor), Damjan Klobčar (Komentor)

Povzetek

Aluminijeve zlitine so zaradi dobrih fizikalnih in mehanskih lastnosti uveljavljene v najzahtevnejših inženirskih aplikacijah. Hkrati razvoj novih tehnologij varjenja omogoča spajanje visoko-trdnostnih aluminijevih zlitin, ki so s konvencionalnimi postopki izredno težko varive, in ponuja najrazličnejše raziskave mehanskih lastnosti ter razmer v takih zvarnih spojih. V zaključni nalogi smo zato analizirali longitudinalne zaostale napetosti v spojih raznorodnih visoko-trdnostnih aluminijevih zlitin 7075-T651 in 2017A-T451. S postopkom varjenja z gnetenjem smo uspešno izdelali šest vzorčnih spojev, z različnimi varilnimi parametri. V nadaljevanju smo v izbranih merilnih mestih z metodo rentgenske difrakcije izmerili zaostale napetosti v vzdolžni smeri glede na potek varjenja. Na podlagi izvedenih meritev smo ovrednotili grafe porazdelitve zaostalih napetosti ter dokazali, da so zaostale napetosti v območju spoja pozitivne, tj. natezne, ki pa z odmikom od zvara preidejo v tlačne. Ugotovili smo tudi, da so večji ekstremi zaostalih napetosti prisotni na nazadujoči strani zvarov, pri čemer smo najvišje vrednosti izmerili v vzorcu, zvarjenem z najvišjo podajalno hitrostjo.

Ključne besede

diplomske naloge;aluminijeve zlitine;varjenje z gnetenjem;zaostale napetosti;rentgenska difrakcija;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [A. Smolej]
UDK: 621.791:669(043.2)
COBISS: 16235547 Povezava se bo odprla v novem oknu
Št. ogledov: 1733
Št. prenosov: 285
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Longitudinal residual stresses in high-strength aluminium alloy welds
Sekundarni povzetek: Aluminium alloys are established in the most demanding engineering applications because of good physical and mechanical characteristics. At the same time the development of new welding technologies enables joining of high-strength aluminium alloys, which are hard to weld by conventional fusion welding. This offers different researches of mechanical properties and circumstances in such weld joints. In the final project paper we therefore analysed longitudinal residual stresses in joints of dissimilar high-strength aluminium alloys 7075-T651 and 2017A-T451. With the friction stir welding procedure we successfully created six sample joints with different welding parameters. Further, in selected measuring points longitudinal residual stresses according to the welding direction were measured by the method of x-ray diffraction. On the basis of performed measurements we evaluated the distribution graphs of residual stresses and proved that the residual stresses in the stir-zone are positive, that is tensile. By moving away from the weld joint tensile residual stresses become compressive stresses. We also found out that bigger extremes of residual stresses are present on the retreating side and the highest values were measured in the specimen welded with the highest rotation rate.
Sekundarne ključne besede: alluminium alloys;friction stir welding;residual stresses;x-ray diffraction;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, 41 f.
ID: 10959627
Priporočena dela:
, zaključna naloga univerzitetnega študijskega programa I. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, diplomska naloga visokošolskega strokovnega študijskega programa I. stopnje strojništvo
, zaključna naloga univerzitetnega študijskega programa I. stopnje Strojništvo