Uroš Trdan (Avtor), Matej Hočevar (Avtor), Peter Gregorčič (Avtor)

Povzetek

This work investigates the evolution from superhydrophilic to superhydrophobic surface state on corrosion behaviour of SS316L produced by Nd:YAG nanosecond direct laser texturing (DLT). Results confirm perfect correlation among wettability and corrosion, hence superhydrophobic surface with a contact angle of 168 +/- 3.0° reflects in enhanced passivity, lower anodic dissolution and corrosion current reduction. Characterization of the corrosion attack by 3D microscopy reveals high sensitivity of superhydrophilic surfaces on corrosion propagation direction in regard to the laser beam passage (90°/0°). However, this trend completely diminishes with superhydrophobic development. Further, DLT also completely prohibits intergranular corrosion detected with the non-processed sample.

Ključne besede

lasersko teksturiranje;nerjavno jeklo;polarizacija;interkristalna korozija;pasivacija;jamičasta korozija;stainless steel;polarization;SEM;intergranular corrosion;passivity;pitting corrosion;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UL FS - Fakulteta za strojništvo
UDK: 620.178.3:621.7(045)
COBISS: 15482907 Povezava se bo odprla v novem oknu
ISSN: 0010-938X
Št. ogledov: 735
Št. prenosov: 856
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: lasersko teksturiranje;nerjavno jeklo;polarizacija;interkristalna korozija;pasivacija;jamičasta korozija;
Vrsta dela (COBISS): Članek v reviji
Strani: str. 21-26
Zvezek: ǂVol. ǂ123
Čas izdaje: Jul. 2017
DOI: 10.1016/j.corsci.2017.04.005
ID: 10991032