diplomsko delo
Anže Bajželj (Avtor), Iztok Naglič (Mentor)

Povzetek

Namen diplomskega dela je karakterizacija mikrostrukture in mehanskih lastnosti nerjavnih jekel 08X14NDL in GX4CrNi13-4. Karakterizacija mehanskih lastnosti je potekala s pomočjo nateznega preizkusa, merjenja trdote in udarne žilavosti, karakterizacija mikrostrukture pa s pomočjo svetlobne mikroskopije, rentgenske fazne analize (XRD), vrstične elektronske mikroskopije (SEM), energijsko disperzijske spektroskopije (EDS) in izračunov ravnotežnih faznih diagramov za preiskovana jekla. Mikrostruktura jekel 08X14NDL in GX4CrNi13-4 je sestavljena pretežno iz popuščenega martenzita in δ-ferita. Delež δ-ferita se med toplotno obdelavo ne spreminja in znaša 18,7 % za jeklo 08X14NDL in 2,6 % za jeklo GX4CrNi13-4. S pomočjo mikrokemijske analize EDS je bilo ugotovljeno, da δ-ferit v obeh jeklih vsebuje predvsem večji delež kroma in manjši delež niklja kakor martenzit. Mehanske lastnosti jekla GX4CrNi13-4 so dosegale zahteve standarda, pri jeklu 08X14NDL pa so bile trdote prenizke glede na zahteve standarda. Mikrotrdota δ-ferita je bistveno manjša od mikrotrdote martenzita. Z ustrezno kemično sestavo bi v jeklu 08X14NDL lahko zmanjšali delež mehkejšega δ-ferita.

Ključne besede

mehanske lastnosti;mikrostruktura;martenzitna nerjavna jekla;08X14NDL;GX4CrNi13-4;delta;-ferit;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
Založnik: [A. Bajželj]
UDK: 669
COBISS: 1778527 Povezava se bo odprla v novem oknu
Št. ogledov: 989
Št. prenosov: 318
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: mechanical properties and microstructure of martensitic stainless steels 08X14NDL and GX4CrNi13-4
Sekundarni povzetek: The main purpose of the diploma work was characterization of microstructure and mechanical properties of 08X14NDL and GX4CrNi13-4 martensitic stainless steels. Mechanical properties were characterized by tensile testing, hardness testing and impact toughness testing. Microstructure was characterized by using light microscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive spectroscopy (EDS) and calculation of equilibrium phase diagrams. Microstructure of 08X14NDL and GX4CrNi13-4 steels is composed of martensite and δ-ferrite. The volume fraction of δ-ferrite is 18.7 % for the 08X14NDL steel and 2.6 % for the GX4CrNi13-4 steel and does not change markedly during the process of the heat treatment. EDS microanalysis shows that δ-ferrite in both alloys contains more chromium and less nickel than the martensite. The mechanical properties of the GX4CrNi13-4 steel have met the requirements of the standard while in the case of the 08X14NDL steel the hardness was lower than required. Microhardness of δ-ferrite is significantly lower than the microhardness of martensite. The content of δ-ferrite with lower hardness could be reduced by a proper chemical composition of the 08X14NDL steel.
Sekundarne ključne besede: mechanical properties;microstructure;martensitic stainless steels;08X14NDL;GX4CrNi13-4;delta;-ferrite;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Komentar na gradivo: Univ. v Ljubljani, Naravoslovnotehniška fak. , Odd. za materiale in metalurgijo
Strani: XI, 32 f.
ID: 10994942