magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
Sebastjan Nabergoj (Avtor), Mitjan Kalin (Mentor)

Povzetek

V magistrskem delu je obravnavana problematika obrabe brizgalnega orodja pri brizganju polimera z vsebnostjo steklenih vlaken. Izdelana je podrobna analiza literature, na kateri temelji eksperimentalni del, kjer je obravnavana obrabna obstojnost štirih kavitetnih vložkov različnih toplotnih obdelav in materialov na delovanje taline polimera. Delo temelji na predpostavki, da je stopnja obrabe v posameznih conah kavitetnih votlin različna. Eksperimentalni del naloge je bil izveden na prototipnem orodju, v katerega so bili vgrajeni omenjeni kavitetni vložki. Testiranje je zajemalo 10 000 brizgov, kot brizgani material pa je bil uporabljen termoplast PA66 GF35. Kvantitativni popis stopnje obrabe je izveden s stopnjo hrapavosti Ra in Rz. Za preučevanje prisotnih obrabnih mehanizmov je uporabljena optična mikroskopija in interferomatrija. Največja stopnja obrabe je bila zaznana na ustju kavitetnih vložkov, ki se odraža v popačenju njegove geometrije. Zaznane so bile tudi različne obrabne obstojnosti uporabljenih materialov in toplotnih obdelav.

Ključne besede

magistrske naloge;obraba;kaviteta;steklena vlakna;cona;brizgalno orodje;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [S. Nabergoj]
UDK: 621.9:678.027.74:677.521(043.2)
COBISS: 16923675 Povezava se bo odprla v novem oknu
Št. ogledov: 1264
Št. prenosov: 290
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Wear of injection mold for glass fiber reinforced polymer
Sekundarni povzetek: The masterʼs thesis deals with the problem of the injection mould wear in the process of injecting glass reinforced polymer. The thesis presents a detailed analysis of literature upon which the experimental part is based, where the wear resistance of four cavity inserts of various heat treatments and materials is considered. The work is based upon assumption of a different degree of wear in individual cavity zones. The experimental part was performed on a prototype injection mould in which the said cavity inserts were installed. The test involved 10 000 shots of PA66 GF35 thermoplastic material. Wear rates are quantified with Ra and Rz roughness parameters before and after the experiment was conducted. Optical microscopy and interferometry were also used to observe present wearing mechanisms. The highest wear rate was detected in the region of the tunnel gates of the cavity inserts, which is reflected in the distortion of their geometry. Different wear durability was detected at different materials and heat treatments.
Sekundarne ključne besede: master thesis;wear;cavity;glass fibre;zone;injection mould;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. Ljubljana, Fak. za strojništvo
Strani: XXVI, 115 str.
ID: 11219417
Priporočena dela:
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program