zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
Anže Trifković (Avtor), Roman Šturm (Mentor)

Povzetek

V zaključni nalogi smo s trdninskim, pulznim Nd:YAG laserjem lasersko pretaljevali toplotno obdelano aluminijevo zlitino 7075-T6 in obravnavali vpliv velikosti pege laserskega žarka in moči laserja na globino penetracije in spremembo trdote pretaljene površine v primerjavi z osnovnim materialom. Izmerili smo tudi nastale zaostale napetosti v vzorcu. Dokazali smo, da gostota energije laserskega žarka nima bistvenega vpliva na doseženo trdoto pretaljene površine. Mikrostruktura se je spremenila v finozrnato, trdota pa se je glede na dobavljeno kvaliteto Al 7075-T6 zmanjšala. Če bi uporabili zlitino Al 7075-T0, ki ni predhodno toplotno obdelana s staranjem, bi se trdota povečala. V posameznih sledeh laserskega žarka so zaostale napetosti opazno večje, kot pa v večji pretaljeni površini, ki smo jo dobili s prekrivanjem sledi.

Ključne besede

diplomske naloge;lasersko pretaljevanje;aluminijeve zlitine;zaostale napetosti;trdota;mikrostruktura;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [A. Trifković]
UDK: 621.785.54:669.715(043.2)
COBISS: 16952347 Povezava se bo odprla v novem oknu
Št. ogledov: 975
Št. prenosov: 190
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Laser melting of aluminium alloy 7075
Sekundarni povzetek: In the final thesis, we used a solid-state, pulsed Nd:YAG laser to melt heat-treated aluminum alloy 7075-T6 and discussed the influence of the laser beam spot size and the laser's power on the penetration depth and change in the hardness of the treated surface compared to the base material. Residual stresses in the sample were also measured. We have demonstrated that the laser beam energy density does not have a significant effect on the attained hardness of the melted surface. The microstructure turned into fine-grained, and the hardness decreased in terms of the delivered Al 7075-T6 quality. If an Al 7075-T0 alloy, not pre-treated with aging, had been used, the hardness would have increased. In the individual traces of the laser beam, the residual stresses are noticeably larger than in the larger melted surface obtained by overlaying the traces.
Sekundarne ključne besede: laser melting;aluminium alloys;residual stress;hardness;microstructure;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, f. 30
ID: 11221994
Priporočena dela:
, zaključna naloga Razvojno raziskovalnega programa I. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo