magistrsko delo
Matej Bizjak (Avtor), Borut Kosec (Mentor)

Povzetek

Razvoj jekel odpornih na lezenje za uporabo pri visokih temperaturah in visokih tlakih, poteka v smeri izboljšanja življenjske dobe materiala in boljših mehanskih ter toplotnih lastnosti. V tem delu smo izmerili toplotno prevodnost malolegiranega jekla po njegovi dolgotrajni uporabi pri povišanih temperaturah. Meritve smo izvedli na napravi Hot Disk TPS 2200 po standardu ISO 22007-2 iz skupine standardov ISO 22007. Toplotno prevodnost jekla smo merili pri sobni temperaturi, pri 290 °C in pri 400 °C. Opravili smo tudi analizo mikrostrukture na vrstičnem elektronskem mikroskopu in svetlobnem mikroskopu ter analize kemične sestave z XRF in EDS metodo.

Ključne besede

jeklo za termoenergetiko;toplotne lastnosti;meritve toplotne prevodnosti;jekla odporna na lezenje;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
Založnik: [M. Bizjak]
UDK: 669
COBISS: 1845855 Povezava se bo odprla v novem oknu
Št. ogledov: 600
Št. prenosov: 264
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: determination of thermal properties of steel for thermoenergetics
Sekundarni povzetek: Research and development of creep resistant steels for use in high pressure and high temperature environments is based on endeavours to extend the lifetime of material, reduce the cost of maintenance and to improve thermal and mechanical properties of material. In this master’s thesis we discuss the measurements of thermal conductivity conducted on specimens of low alloyed creep resistant steel after use under elevated temperatures in Thermoenergetics. Measurements were performed on the instrument Hot Disk TPS 2200 in accordance to standard ISO 22007-2 from the group of standards ISO 22007. Thermal conductivity was measured at room temperature, at 290 °C and at 400 °C. Microstructure analysis of the steel sample was performed on SEM electron microscope as well as on light microscope. With XRF and EDS methods we also analysed the chemical composition of the steel.
Sekundarne ključne besede: steel for thermoenergetics;thermal conductivity;creep resistant steels;thermal properties;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Naravoslovnotehniška fak., Odd. za materiale in metalurgijo
Strani: XV, 51 f.
ID: 11232967