diplomski projekt
Blaž Lešnjak (Avtor), Franc Pohleven (Recenzent), Miha Humar (Mentor)

Povzetek

Termična modifikacija lesa je eden izmed najbolj perspektivnih postopkov zaščite lesa. Uporaba tega postopka se širi iz leta v leto. Postopek je okolju prijazen, saj poteka brez dodanih kemikalij. Les modificiramo pri temperaturah od 170 °C v posebnih komorah, brez prisotnosti kisika. Z razmerjem med trajanjem modifikacije in temperaturo modifikacije, dosežemo želeno stopnjo zaščite. Z višjo temperaturo dobimo bolj odporen les, a hkrati zmanjšamo njegove mehanske lastnosti. Večina raziskav je bila opravljena na industrijsko pomembnih lesnih vrstah, manj uporabljene lesne vrste pa so manj raziskane. Štiri različne manj pomembne lesne vrste (macesen, topol, jelša in jesen) smo testirali pri različnih temperaturah in različnem trajanju modifikacije. Vzorcem smo določili izgubo mase po modifikaciji in jih izpostavili štirim vrstam gliv (Trametes versicolor, Pleurotus ostreatus, Gloeophyllum trabeum, Antrodia vaillanti) ter jih za 16 tednov postavili v inkubator. Iz gravimetrično določene izgube mase smo ugotovili, da je odpornost lesa proti glivam v linearni povezavi z izgubo mase med termično modifikacijo. Nižja temperatura (do 190 °C) v nobenem primeru ne zadošča za popolno zaščito, medtem ko se višja temperatura (215 °C) že izkaže za učinkovito zaščito, vendar ne proti vsem vrstam lesnih gliv.

Ključne besede

les;termična modifikacija;temperatura;glive;odpornost;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [B. Lešnjak]
UDK: 630*841
COBISS: 2370697 Povezava se bo odprla v novem oknu
Št. ogledov: 259
Št. prenosov: 52
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Fungicidal properties of less known thermal modified wood species
Sekundarni povzetek: Thermal modification of wood is one of the most perspective procedures to protect wood. The use of this procedure is expanding from year to year. The process is environmentally friendly as it runs without any added chemicals. Wood is modified at temperatures from 170 °C to 240 °C in special chambers, without the presence of oxygen. By relationship between the duration of modification and the temperature of modification, the desired level of protection is achieved. Higher temperature makes the timber more resistant, but at the same time, it reduces mechanical properties. Most researchers have been done on the important industrial wood species; less used timber species are less researched. Four different, less commercially important timber species (larch, poplar, alder and ash), were tested at different temperatures and different duration. The samples were determined by weight loss, modified using four different fungi (Trametes versicolor, Pleurotus ostreatus, Gloeophyllum trabeum, Antrodia vaillanti), and placed for 16 weeks in an incubator. From gravimetrically determined weight loss, we found out that the resistance of wood against fungi is in linear relation to the weight loss during the thermal modification. Lower temperature (up to 190 °C) is in no case sufficient for complete protection, while higher temperature (up to 215 °C) already proves to be effective, but not against all types of wood fungi.
Sekundarne ključne besede: wood;thermal modification;temperature;fungi;durability;
Vrsta dela (COBISS): Delo diplomskega projekta/projektno delo
Komentar na gradivo: Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: VIII, 37 f.
ID: 11920730