Iz titanovega tetraklorida sem sintetizirala tridimenzionalne rožicam podobne mikrodelce TiO2, ki sem jih uporabila za pripravo treh različnih suspenzij. Suspenzije sem v različnem številu slojev nanesla na steklene ploščice in jih termično obdelala. Ploščice sem nato uporabila za fotokatalitsko razgradnjo barvila Plasmocorinth B v šaržnem reaktorju s svetlobo z valovanjem v območju ultravijoličnega spektra pri različnih pogojih. Fotokatalitsko razgradnjo barvila sem preverjala z merjenjem absorbance vzorcev s spektrofotometrom. Z vrstičnim elektronskim mikroskopom smo posneli ploščice z nanosi za podrobnejši vpogled v površino in strukturo nanosov suspenzije. Rezultati so pokazali, da se je za najboljše vezivno sredstvo izkazal polivinilpirolidon, saj je suspenzija s tem dodatkom v obliki plasti po termični obdelavi najhitreje razgrajevala barvilo. Razgradnjo barvila so dodatno pospešili trije nanosi suspenzije in prepihovanje vodne raztopine barvila s kisikom.

Ključne besede

titanov dioksid;mikrodelci;fotokataliza;reaktorji za fotokatalizo;UV svetloba;polprevodniki;polivinilpirolidon;spektrofotometrija;diplomske naloge;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [M. Klemenić]
UDK: 546.82-31:544.526.5(043.2)
COBISS: 27430659 Povezava se bo odprla v novem oknu
Št. ogledov: 428
Št. prenosov: 87
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Immobilization of TiO2 nanostructured microparticles
Sekundarni povzetek: Titanium tetrachloride was used as a precursor for the synthesis of three-dimensional flower-like TiO2 microparticles, from which three different suspensions were further prepared. The suspensions were deposited in a different number of layers to the glass slides, which were then heat-treated. The prepared plates were used for the photocatalytic degradation of Plasmocorinth B in a batch reactor under UV light and under different conditions. The photocatalytic degradation of the dye was checked by measuring the absorption of the samples with a spectrophotometer. A detailed insight into the morphology and structure of the photocatalyst was obtained with the scanning electron microscope. The results showed that polyvinylpyrrolidone proved to be the best binder as the resulting suspension in the form of layers and after heat treatment degrades the dye the fastest. The degradation of the dye was also accelerated by three layers of the suspension deposited on the glass slides and by purging the aqueous dye solution with oxygen.
Sekundarne ključne besede: titanium dioxide;microparticles;photocatalysis;UV light;semiconductor;polyvinylpyrrolidone;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 1000374
Komentar na gradivo: Univ. v Ljubljani, Fak. za kemijo in kemijsko tehnologijo
Strani: 28 str.
ID: 12006066