diplomsko delo
Rok Poljanc (Avtor), Marjan Marinšek (Mentor)

Povzetek

Beton je zgodovinsko gledano eden najbolj pomembnih in uporabljenih materialov in ravno zaradi tega je njegovo propadanje zelo velik problem. Za njegovo preprečitev pa je potrebno razumeti različne vzroke propadanja betona. Največji delež k propadanju betona gre prepisati naravnim in kemijskim dejavnikom. Alkalno-karbonatna reakcija spada med kemijske reakcije in s svojim delovanjem omogoča pospešeno propadanje betona. Glavni proces ACR reakcije je dedolomitizacija, ki je sicer neškodljiva, se pa zaradi nje zmanjša prostornina faz in s tem nudi možnost prodiranja ASR gela globje v beton. V diplomski nalogi so predstavljene tudi metode in aparature za določevanje mikrostrukture in različnih tipov faz v procesu propadanja betona zaradi ACR reakcije.

Ključne besede

beton;propadanje;alkalno-agregatna reakcija;alkalno-karbonatna reakcija;ACR;dedolomitizacija;mikrostruktura;diplomska dela;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [R. Poljanc]
UDK: 666.9(043.2)
COBISS: 29787651 Povezava se bo odprla v novem oknu
Št. ogledov: 369
Št. prenosov: 79
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Monitoring of ACR reactions through microstructural analysis of concree with dolomite aggregate.
Sekundarni povzetek: Concrete is historically one of the most important and most used materials in the world. Because of this, its degradation is very big problem. However, to prevent the degradation of concrete, it is necessary to understand the various causes of concrete degradation. Most common reason for degradation of concrete are natural and chemical factors. The alkali-carbonate reaction is type of chemical reaction and its action enables accelerated degradation of the concrete. The main process of the ACR reaction is dedolomitization which is harmless but it reduces the volume of the phases and thus offers the possibility of penetrating the ASR gel deeper into the concrete. The degree paper also presents methods and analytical equipment for determining the microstructure and different types of phases in degradation of concrete due to the ACR reaction.
Sekundarne ključne besede: concrete;dedolomitization;microstructure;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 1000372
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za kemijo in kemijsko tehnologijo, UNI Kemijsko inženirstvo
Strani: 30 str.
ID: 12031174