diplomsko delo
Klara Šifrer (Avtor), Urška Lavrenčič Štangar (Mentor)

Povzetek

Tekom diplomskega dela sem pripravila sol titanovega dioksida po anorganski sintezni poti iz TiCl4 z dodatkom NH4NO3 in hidroksipropil celuloze. Z dušikom dopirane fotokatalitsko aktivne tanke plasti sem pripravila tako, da sem nastali sol s tehniko potapljanja podlage nanesla na objektna stekla in jih nato termično obdelala pri temperaturi 600 °. Nastale plasti sem uporabila za fotokatalitsko razgradnjo antibiotika oksitetraciklina pod UV svetlobo z valovno dolžino 350 nm. Razgradnjo antibiotika sem spremljala spektrofotometrično na 15 minut; celotni čas fotokatalitske razgradnje pa je bil 3 ure. Razgradnjo onesnažila v vodovodni in deionizirani vodi sem spremljala na osnovi meritev absorpcijskih spektrov učinkovine v območju med 200 in 800 nm. Opazovala sem vpliv pH raztopine in začetne koncentracije onesnažila na hitrost razgradnje. Naredila sem tudi umeritvene krivulje oksitetraciklina v deionizirani in vodovodni vodi, iz katerih lahko iz izmerjene absorbance pri valovni dolžini 355 nm (deionizirana voda) oziroma 375 nm (vodovodna voda) določamo koncentracijo oksitetraciklina v raztopini. Iz meritev absorbcijskih spektrov teh raztopin pred in po triurnem osvetljevanju z UV svetlobo sem lahko določila še spontano razgradnjo oksitetraciklina na UV svetlobi.

Ključne besede

fotokataliza;fotokatalitska razgradnja;titanov dioksid;sol-gel postopek;tanke plasti;antibiotiki v okolju;oksitetraciklin;diplomska dela;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [K. Šifrer]
UDK: 544.526.5:547.82-31:615.33(043.2)
COBISS: 29861379 Povezava se bo odprla v novem oknu
Št. ogledov: 470
Št. prenosov: 87
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Photocatalytic degradation of antibiotic tetracycline by thin films of titanium dioxide
Sekundarni povzetek: During my diploma work, titanium dioxide sol was prepared by inorganic synthesis route from TiCl4 with addition of NH4NO3 and hydroxypropyl cellulose. The prepared sol was deposited onto object glasses by dip-coating technique. After thermal treatment at 600 °C nitrogen-doped photocatalytically active thin films were prepared. These layers were then used for the photocatalytic degradation of the antibiotic oxytetracycline under UV light irradiation with a wavelength of 350 nm. The antibiotic degradation was measured spectrophotometrically every 15 minutes; the total time of photocatalytic degradation was 3 hours. The degradation of the contaminant in tap water and deionized water was monitored, based on the obtained absorption spectra of the active substance in the range between 200 and 800 nm. The influence of the pH of the solution and the initial concentration of the contaminant on the degradation rate was investigated. Calibration curves of oxytetracycline in deionized water and tap water were also constructed, from which the concentration of oxytetracycline in the solution can be determined from the measured absorbance at a wavelength of 355 nm (deionized water) and 375 nm (tap water). From the absorption spectra of these solutions before and after irradiation with UV light for three hours, the spontaneous degradation of oxytetracycline in UV light can also be followed.
Sekundarne ključne besede: titanium dioxide;sol-gel method;thin film;photocatalytic degradation;tetracycline;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 1000373
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za kemijo in kemijsko tehnologijo, UNI Kemija
Strani: 38 str.
ID: 12031329