diplomsko delo
Metod Meolic (Avtor), Janez Kramberger (Mentor), Andrej Ivanič (Komentor)

Povzetek

V okviru diplomskega dela smo izdelali preizkušance iz ogljikovih vlaken in PMI pene, izvedli eksperimentalne preizkuse in jih numerično analizirali. Med posameznimi rezultati je bila izvedena primerjalna analiza z namenom ugotovitve odstopanj med eksperimentalnim delom in zastavljenim numeričnim preračunom. V začetku naloge je opisan material, iz katerega so bili preizkušanci izdelani. Sledi opis postopka priprave in izdelave vseh tipov preizkušancev s pripadajočimi tehnologijami. Preizkušanci so se med seboj razlikovali v orientiranosti plasti karbonskih vlaken. Zunanje dimenzije so bile v vseh primerih konstantne. Preizkušance smo upogibno preizkusili v laboratoriju na trgalnem stroju. Po izvedbi preizkusov smo zastavili numerični model preizkušancev. Po obdelavi podatkov dobljenih iz eksperimentalnega in numeričnega dela smo ugotovili, da se preizkušanci v elastičnem področju ujemajo z odstopanjem v velikostnem razredu 20 odstotkov. V sklepnem delu so predstavljene možnosti za nadaljnje raziskovanje in razvoj numeričnih materialnih modelov.

Ključne besede

ogljikova vlakna;kompozit;izdelava;numerična simulacija;diplomske naloge;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: [M. Meolic]
UDK: 620.168:[620.174+519.876.5](043.2)
COBISS: 52972035 Povezava se bo odprla v novem oknu
Št. ogledov: 469
Št. prenosov: 52
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Experimental and numerical analysis of carbon beams
Sekundarni povzetek: As part of the diploma thesis, we made test specimens from carbon fiber and PMI foam, performed tests and numerically analyzed them in the elastic field. A comparative analysis was carried out between the individual results in order to determine the deviations between the experimental part and the set numerical calculation. At the beginning of the thesis, the material from which the test specimens were made is described. The following part is a description of the process of preparation and manufacture of all test specimens types with associated technologies. The test specimens differed from each other in the orientation of the carbon fiber layers and the external dimensions were constant in all cases. A bending test was carried out on the test specimens in the laboratory on an adapted tensile-testing machine. After carrying out the tests, we set a numerical model of the test specimens, which we had previously made, and of the bending test. After processing the data obtained from the experimental and numerical part, we found that the elastic region of the test specimens matched the deviation in the size class 20 percent. The concluding part presents the possibilities for further research and development of numerical material models.
Sekundarne ključne besede: carbon fiber;composites;manufacture;numerical simulation;
Vrsta dela (COBISS): Diplomsko delo/naloga
Komentar na gradivo: Univ. v Mariboru, Fak. za strojništvo, Konstrukterstvo
Strani: VII, 34 f.
ID: 12038244