diplomsko delo
Tea Lovrić (Avtor), Iztok Naglič (Mentor)

Povzetek

Diplomsko delo obravnava karakterizacijo mikrostrukture zlitin iz sistema Cu-Ni-Sm. V elektroobločni peči smo izdelali štiri vzorce zlitin z 10 at. % (Cu80Ni10Sm10 in Cu60Ni30Sm10) in s 30 at. % Sm (Cu60Ni10Sm30 in Cu40Ni30Sm30) ter jih toplotno obdelali pri 500 oC. Karakterizacijo mikrostruktur smo izvedli tako na svetlobnem kot tudi na vrstičnem elektronskem mikroskopu, kjer smo poleg opazovanja mikrostruktur z metodo EDS ugotavljali tudi kemijsko sestavo faz. Za zanesljivo potrditev prisotnih faz v zlitinah smo uporabili še rentgensko fazno analizo. Rezultati karakterizacije vzorcev Cu80Ni10Sm10 in Cu60Ni30Sm10 so pokazali, da sta v mikrostrukturi prisotni fazi ?Cu in (Cu,Ni)5Sm. Mikroanaliza z EDS je pokazala, da znaša vsebnost samarija v ?Cu fazi 0,3 at. % v zlitini Cu80Ni10Sm10 in 0,8 at. % v zlitini Cu60Ni30Sm10. Elektronski posnetki mikrostrukture so pokazali, da sta v zlitini Cu60Ni10Sm30 prisotni dve fazi, v zlitini Cu40Ni30Sm30 pa tri faze. Z rentgensko fazno analizo smo potrdili zgolj prisotnost faze (Cu,Ni)2Sm.

Ključne besede

zlitinski sistem Cu-Ni-Sm;mikrostruktura;mikroanaliza EDS;rentgenska difrakcija;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
Založnik: [T. Lovrić]
UDK: 669
COBISS: 32984067 Povezava se bo odprla v novem oknu
Št. ogledov: 401
Št. prenosov: 87
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: characterization of phases in the Cu-Ni-Sm system
Sekundarni povzetek: Diploma thesis deals with the characterization of the microstructure of Cu-Ni-Sm alloy system. Four alloys with 10 at. % (Cu80Ni10Sm10 and Cu60Ni30Sm10) and with 30 at. % Sm (Cu60Ni10Sm30 and Cu40Ni30Sm30) were prepared in an arc melting furnace and heat-treated at 500 ºC. The characterization of microstructures was performed by light microscopy, scanning electron microscopy, energy dispersive X-ray spectroscopy (EDS) microanalysis and X-ray diffraction. It was found that αCu and (Cu,Ni)5Sm phases were present in both Cu80Ni10Sm10 and Cu60Ni30Sm10 alloys. Microanalysis EDS shows that the content of samarium in the αCu phase is 0.3 at. % in Cu80Ni10Sm10 and 0.8 at. % in Cu60Ni30Sm10. Electronic micrographs show presence of two phases in Cu60Ni10Sm30 alloy and three in the Cu40Ni30Sm30 alloy. X-ray diffraction confirms the presence of only the (Cu,Ni)2Sm phase in both alloys.
Sekundarne ključne besede: Cu-Ni-Sm alloy system;microstructure;EDS microanalysis;X-ray diffraction;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Naravoslovnotehniška fak., Oddelek za materiale in metalurgijo
Strani: XI, 33 f.
ID: 12046530