Cilj magistrske naloge je bil izdelava in testiranje vseceluloznih kompozitov iz celuloznih vlaken in nanofibrilirane celuloze. Za izdelavo kompozitov smo uporabili tri unikatne metode, ki so bile plod preliminarnih testov. Pri papirniški metodi, smo celulozno maso in nanofibrilirano celulozo zmešali in iz zmesi formirali kompozit, med tem ko smo pri metodi z lijem in metodi s filmi nanocelulozo nanašali na že narejene celulozne liste. Pri papirniški metodi je šlo torej za izdelavo homogenega kompozita, med tem ko smo pri drugih dveh metodah nanocelulozo nanesli le na površino. Z vsako metodo smo izdelali kompozite z različnimi dodatki nanoceluloze ter tako preverili vpliv dodatka na mehanske lastnosti in poroznost kompozita. V analitskem laboratoriju smo kompozitom izmerili gramaturo, debelino, utržno jakost, poroznost in permeabilnost ter raztržno odpornost. Rezulate smo premerjali glede na dodatek nanoceluloze in med samimi metodami.

Ključne besede

celuloza;nanoceluloza;papir;kompozit;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [M. Pongrac]
UDK: 630*812:547.458.8
COBISS: 81177347 Povezava se bo odprla v novem oknu
Št. ogledov: 182
Št. prenosov: 32
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Mechanical properties and porosity of biobased composite from woody cellulose fibers and nanofibrills
Sekundarni povzetek: The goal of this research was to produce and test all cellulose composites from cellulose fibres and nanofibrilated cellulose. For the production of the composites we used three unique methods which were the result of extensive preliminary tests. The papermaking method was based on mixing cellulose fibres with nanofibrilated cellulose and forming a composite on the mesh, while the funnel and film method used already made cellulose sheets and coated them with nanofibrilated cellulose. For every method we made composites with different contents of nanofibrilated cellulose and tested its impact on the mechanical properties and porosity. We measured the grammage, thickness, tensile strength, porosity and tear resistance. The results were compared based on the amount of additive and method used.
Sekundarne ključne besede: cellulose;nanocellulose;paper;composite;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Komentar na gradivo: Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: IX, 53 f.
ID: 13723037