Franc Zupanič (Avtor), Elfride Unterweger (Avtor), Albert C. Kneissl (Avtor), Ivan Anžel (Avtor), Gorazd Lojen (Avtor)

Povzetek

This work investigates the possibilities for applying a focussed ion beam (FIB) for the metallographic preparation and characterization of Cu-Al-Ni melt-spun ribbons. Two alloys were selected for this reason: CuAl13Ni4 and CuAl15Ni4. The microstructure of the first alloy was fully martensitic and the microstructure of the second consisted of two phases: martensite and ▫$\gamma_2$▫. It was discovered that with FIB-etching the microstructures of both alloys can be clearly revealed on polished cross-sections of the melt-spun ribbons, as well as on their wheel-side and air-side surfaces. However, better results were obtained when the etched surface was smoother, and finer details were visible when using smaller ion currents. In addition, a study was made into the influence of platinum deposition on the quality of 3D-cross sections. It was found that Pt-deposition is necessary when the edge of the trench should be straight and sharp, and the surface of the 3D cross-section smooth. However, in this case, the microstructure of the ribbons free surface cannot be seen.

Ključne besede

focussed ion beam;FIB;metallography;melt-spinning;shape memory alloy;Cu-Al-Ni;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 669
COBISS: 12060182 Povezava se bo odprla v novem oknu
ISSN: 1408-7073
Matična publikacija: RMZ - Materials and geoenvironment
Št. ogledov: 1255
Št. prenosov: 24
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni naslov: Karakterizacija hitrostrjenih trakov zlitine Cu-Al-Ni z uporabo fokusiranega ionskega curka
Sekundarni povzetek: V tem delu smo raziskali mo.nosti uporabe fokusiranega ionskega curka (FIB) pri metalografski pripravi in karakterizaciji hitro strjenih zlitin Cu-Al- Ni. Izbrali smo dve zlitini: CuAl13Ni4 in CuAl15Ni4. Mikrostruktura prve zlitine je bila v celoti martenzitna, medtem ko je bila mikrostruktura druge zlitine sestavljena iz dveh faz: martenzita in ▫$\gamma_2$▫. Ugotovljeno je bilo, da lahko pri jedkanju z ionskim curkom odkrijemo mikrostrukturo tako na poliranih prečnih prerezih trakov, kot tudi na obeh prostih površinah hitrostrjenih trakov. Mikrostruktura se je boljše odkrila, če je bila raziskana površina bolj gladka, medtem ko smo lahko razločili drobnejše mikrostrukturne sestavine pri uporabi manjših ionskih tokov. Poleg tega smo študirali tudi vpliv nanosa platine na kakovost 3D-prečnih prerezov. Ugotovili smo, da je nanos platine smiselno uporabiti, če želimo zelo ravne in ostre robove reza ter gladko površino prečnega reza, vendar pa v tem primeru ne moremo videti mikrostrukture proste površine.
Sekundarne ključne besede: fokusiran ionski curek;FIB;metalografija;litje na vrteče kolo;zlitina z oblikovnim spominom;
URN: URN:NBN:SI
Strani: str. 319-329
Letnik: ǂVol. ǂ54
Zvezek: ǂno. ǂ3
Čas izdaje: 2007
Ključne besede (UDK): applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;chemical technology;chemical and related industries;kemijska tehnologija;kemijske in sorodne industrije;metallurgy;metalurgija;
ID: 1437559