diplomsko delo univerzitetnega študijskega programa I. stopnje
Vita Trkulja (Avtor), Peter Krajnc (Mentor), Muzafera Paljevac (Komentor)

Povzetek

V diplomskem delu z naslovom Odstranjevanje organskih polutantov iz vode s poroznimi polielektroliti smo sintetizirali vzorce poliakrilne kisline z različnimi stopnjami zamreženosti. Zanimalo nas je, kakšen vpliv ima zamreženost polimernega materiala na njegove adsorptivne lastnosti. Monolite poliakrilne kisline smo pridobili s postopkom polimerizacije kontinuirne faze emulzije z visokim deležem notranje faze. Za pripravo smo uporabili monomer akrilne kisline, zamreževalo N,N' – metilenbisakrilamid, deionizirano vodo, surfaktant Triton X – 405, natrijev hidroksid in iniciator amonijev persulfat. Dodali smo tudi toluen, ki je predstavljal notranjo fazo emulzije, in redoks iniciator N,N,N',N' – tetrametilenetilendiamin. Ker ob dodatku natrijevega hidroksida nastane sol akrilne kisline, smo enega izmed monolitov sintetizirali brez dodatka, saj nas je zanimalo kakšen vpliv ima to na sposobnosti adsorpcije. Reakcija, ki je potekla, je bila prosta verižna radikalska polimerizacija kontinuirne faze emulzije z visokim deležem notranje faze tipa olje v vodi. Kot končne produkte smo dobili monolite z naslednjimi stopnjami zamreženosti: 10,9 mol%, 18,5 mol%, 25,0 mol% in 30,6 mol%. En monolit smo sintetizirali s 9,8 mol% zamreženostjo in brez dodatka natrijevega hidroksida. Preden smo izvedli karakterizacijo, smo vzorce očistili v Soxhletovem aparatu, kjer smo ekstrahirali nezreagirane reaktante. Po čiščenju smo monolite shranili v metanolu, pred samo izvedbo meritev absorpcije pa smo metanol zamenjali z deionizirano vodo, saj smo meritve izvajali z vodnimi raztopinami barvil. Ugotovili smo, da ima takšen material veliko boljše sposobnosti adsorpcije za barvilo metilen modro kot metiloranž. Del materiala smo posušili, ker smo meritve izvajali pri suhih in mokrih vzorcih. Rezultati kažejo, da je adsorpcija za barvilo metilen modro boljša pri mokrih vzorcih kot pri suhih.

Ključne besede

poliakrilna kislina;adsorptivne lastnosti;metiloranž;metilen modro;emulzija;poliHIPE;diplomske naloge;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [V. Trkulja]
UDK: 544.6.018.47-036.5(043.2)
COBISS: 132094467 Povezava se bo odprla v novem oknu
Št. ogledov: 92
Št. prenosov: 12
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Removal of organic pollutants from water using porous polyelectrolytes
Sekundarni povzetek: In the diploma thesis entitled Removal of organic pollutants from water using porous polyelectrolites, samples of polyacrilyc adic with different degrees of crosslinking were synthesized. We were interested in the influence the crosslinking of the polymer material has on the adsorption properties. Monolithic polyacrylic acids were obtained by polymerization of a continuous phase of an emulsion with a high internal phase. For the preparation we needed acrylic acid as the monomer, N,N' – methylenbisacrylamide as the crosslinker, deionized water, surfactant Triton X – 405, sodium hydroxide and the initiator ammonium persulfate. We also added toulene, which represented the internal phase of the emulsion, and redox initiator N,N,N′,N′-tetramethylethylenediamine. Since an acrylic acid salt is formed when sodium hydroxide is added, we syntesized one of the monolits whithout the addition, as we were interested in what effect it has on the adsorption capability. The reaction that took place was a free chain radical polymerization of the continuous phase of an emulsion with a high internal phase of the oil-in-water type. As final products we optained monolyths with the following degrees of crosslinking: 10,9 mol%, 18,5 mol%, 25,0 mol% and 30,6 mol%. We synthesised one monolith with a crosslinking degree of 9,8 mol% without the addition of sodium hydroxide. Before performing the characterization, the samples were purified in a Soxhlet apparatus, where the non-reacted reactants were extracted. After cleaning the monolith was stored in methanol and before the absorption measurments were performed, the methanol was replaced with deionized water, since the measurments were performed with aqueous solutions of the dyes. We found that such a material has much better adsorption capabilities for the dye methylen blue than methyl orange. Part of the material was dried because the measurments were observed on dry and wet samples. The results show that adsorption for methylene blue is better for wet samples than for dry samples.
Sekundarne ključne besede: polyacrylic acid;adsorptive properties;methyl orange;methylen blue;emulsion;poliHIPE;
Vrsta dela (COBISS): Diplomsko delo/naloga
Komentar na gradivo: Univ. v Mariboru, Fak. za kemijo in kemijsko tehnologijo
Strani: 1 spletni vir (1 datoteka PDF (VIII, 30 f.))