Propadanje in trajnostna obnova ovoja stavbne dediščine

doktorska disertacija

Mojmir Uranjek (Avtor), Violeta Bokan-Bosiljkov (Mentor), Matjaž Mikoš (Član komisije za zagovor), Vlatko Bosiljkov (Član komisije za zagovor), Jana Šelih (Član komisije za zagovor), Breda Mirtič (Član komisije za zagovor), Jelka Pirkovič (Član komisije za zagovor), Roko Žarnić (Komentor)

Povzetek

Osnovno izhodišče doktorske disertacije je definirati okvire trajnostne obnove stavbne dediščine, predvsem njenega ovoja kot najbolj izpostavljenega stavbnega sklopa. V okviru raziskav smo se osredotočili na poškodbe, ki bi jih lahko na ovoju povzročile podnebne spremembe in potresna obremenitev. V sklopu laboratorijskih preiskav smo načrtovali in preskušali več sestav malt in injekcijskih mešanic na osnovi apnenega veziva z ali brez mineralnih dodatkov, primernih za obnovo in/ali utrjevanje stavbnega ovoja. Rezultati kažejo ugoden vpliv mineralnih dodatkov, kot so apnenčeva moka, žlindra in tuf na lastnosti malt in injekcijskih mešanic. Na opečnih zidkih, grajenih iz dveh malt razvitih v okviru lastnih raziskav, smo ocenili vpliv izmenjujočih se ciklov zmrzovanja/tajanja na trajnost in nosilnost opečnega ovoja. Zidki iz običajne apnene malte in zidki, zgrajeni iz apnene malte z dodano žlindro, so ne glede na poškodbe, brez posledic na mehanske lastnosti sposobni prenesti vsaj 50 ciklov zmrzovanja/tajanja. Po 150-ih ciklih zmrzovanja/tajanja pa se poškodbe odrazijo na zmanjšanju modulov elastičnosti. V okviru in situ preiskav smo ovrednotili kakovost in učinkovitost izbranega utrditvenega trajnostnega posega – sistematičnega injektiranja ovoja kamnite stavbe s cementnimi in cementno-apnenimi injekcijskimi mešanicami. Nelinearna potresna analiza kamnite stavbe, izvedena na osnovi rezultatov in situ preiskav, kaže, da lahko za analizirano vrsto zidov tudi s cementno-apnenimi injekcijskimi mešanicami, ki so za utrjevanje stavbne dediščine primernejše, dosežemo zadostno stopnjo potresne odpornosti.

Ključne besede

gradbeništvo;disertacije;stavbna dediščina;propadanje;zamrzovanje;trajanje;trajnostna obnova;utrjevanje;injektiranje;potresna odpornost;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2011
Tipologija:	2.08 - Doktorska disertacija
Organizacija:	UL FGG - Fakulteta za gradbeništvo in geodezijo
Založnik:	[M. Uranjek]
UDK:	624.042.7:69.059:719(043.3)
COBISS:	5622881
Št. ogledov:	2382
Št. prenosov:	520
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Degradation and sustainable renovation of heritage buildings envelope
Sekundarni povzetek:	The aim of the doctoral dissertation was to define the framework for sustainable renovation of heritage buildings, particularly of the building envelope as the most exposed part. The research was focused on the damage that could be caused by climate change or seismic loads. As a part of the laboratory tests, several mortar and injection grout compositions based on calcium binders with or without mineral additives, suitable for renovation and/or strengthening of the building envelope were designed and tested. It was found that mineral additives such as limestone powder, slag and tuff have a beneficial effect of on the properties of mortars and injection grouts. In continuation, the brick wallets were built with developed mortars and the influence of freeze/thaw cycles on their mechanical properties and durability was evaluated. The wallets built with lime or lime-slag mortar were able to withstand at least 50 freeze/thaw cycles without any effect on their mechanical properties, while after 150 freeze/thaw cycles, the damage was reflected in the reduction of modulus of elasticity. In situ test performed on a stone masonry building enabled us to evaluate the quality and effectiveness of grout injection (using cement or cement-lime grouts) as the chosen sustainable strengthening procedure. The results of the performed seismic analysis based on the experimentally obtained mechanical properties of masonry showed, that in the case of the type of walls under consideration, an adequate level of seismic resistance can be achieved also by using combined cement-lime grouts, which are more suitable for strengthening of heritage buildings.
Sekundarne ključne besede:	civil engineering;doctoral thesis;heritage buildings;degradation;freeze/thaw;sustainable renovation;strengthening;grout injection;seismic resistance;Zgodovinske zgradbe;Disertacije;Zaščita;Arhitekturna dediščina;
URN:	URN:NBN:SI
Vrsta datoteke:	application/pdf
Vrsta dela (COBISS):	Doktorska disertacija
Komentar na gradivo:	Univ. Ljubljana, Fak. za gradbeništvo in geodezijo
Strani:	XXX, 261 str.
ID:	1725409