Nataša Čuk (Avtor), Matjaž Kunaver (Avtor), Sergej Medved (Avtor)

Povzetek

In this study, three-layer particleboards were produced using liquefied wood in an adhesive mixture. The influence of two different formaldehyde resins: melamine-formaldehyde and melamine-urea-formaldehyde resin and two various catalysts: ammonium sulfate and ammonium formate on the particleboard properties was investigated. There were also two pressing parameters examined: temperature and time. The following physical and mechanical properties of particleboards were measured: board thickness, density, moisture content, bending strength and modulus of elasticity, internal bonding strength, surface soundness, thickness swelling and formaldehyde content. The results showed that properties of produced particle boards were better when melamine-formaldehyde resin and ammonium formate as a catalyst were used in combination with liquefied wood in the adhesive mixture. Also, mechanical properties were improved as the press time and press temperature increased. The optimal mechanical properties of particleboards made with the utilization of the liquefied wood in the adhesive mixture were achieved at 3 min press time and 180 °C press temperature using melamine-formaldehyde resin and 3 % of ammonium formate as a catalyst. A very important characteristic is the low formaldehyde content and that is extremely important in the provision of better quality of life. With the liquefaction of wood and the application of liquefied wood in the particleboard production wood biomass exploitation could be significantly increased. We are able to produce new materials from renewable resources that can be a great alternative to the raw materials, originating from crude oil.

Ključne besede

liquefied wood;renewable resources;particleboards;mechanical properties;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UL BF - Biotehniška fakulteta
Založnik: Inštitut za kovinske materiale in tehnologije
UDK: 678:674.07:620.17
COBISS: 859818 Povezava se bo odprla v novem oknu
ISSN: 1580-2949
Št. ogledov: 1170
Št. prenosov: 285
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni naslov: Lastnosti ivernih plošč, izdelanih z uporabo lepila z dodanim utekočinjenim lesom
Sekundarni povzetek: Izdelali smo trislojne iverne plošče, kjer smo za pripravo lepila uporabili utekočinjen les. Ugotavljali smo, kako v kombinaciji z utekočinjenim lesom na lastnosti ivernih plošč vplivata dve različni formaldehidni smoli: melamin-formaldehidna in melamin-urea-formaldehidna smola, ter dva različna katalizatorja: amonijev sulfat in amonijev formiat. Ugotavljali smo tudi vpliv dveh parametrov stiskanja, in sicer temperature stiskanja in časa stiskanja. Fizikalne in mehanske lastnosti, ki smo jih ivernim ploščam določili, so bile: debelina plošče, gostota, vsebnost vlage, upogibna trdnost in modul elastičnosti, razslojna trdnost, čvrstost površine, debelinski nabrek in vsebnost prostega formaldehida. Rezultati so pokazali, da smo izboljšali lastnosti ivernih plošč, ko smo v kombinaciji z utekočinjenim lesom uporabili melamin-formaldehidno smolo in amonijev formiat kot katalizator. Ugotovili smo tudi, da so se lastnosti izdelanih ivernih plošč s časom in temperaturo stiskanja izboljšale. Optimalne lastnosti ivernih plošč, pri katerih smo lepilni mešanici dodali utekočinjen les, smo dosegli pri času stiskanja 3 min in temperaturi stiskanja 180 °C, pri uporabi melamin-formaldehidne smole in 3 % amonijevega formiata kot katalizatorja. Zelo pomembna pri izdelanih ivernih ploščah je tudi majhna vsebnost prostega formaldehida, kar močno vpliva na izboljšanje kvalitete bivanja. Z utekočinjanjem lesa in njegovo uporabo pri izdelavi ivernih plošč povečamo izrabo lesne biomase. Iz obnovljivih virov tako lahko sintetiziramo nove materiale, ki so odlična alternativa materialom, ki jih sicer pridobivamo iz surove nafte.
Sekundarne ključne besede: utekočinjen les;obnovljivi viri;iverne plošče;mehanske lastnosti;
URN: URN:NBN:SI
Vrsta dela (COBISS): Delo ni kategorizirano
Strani: str. 241-245
Letnik: ǂLetn. ǂ45
Zvezek: ǂšt. ǂ3
Čas izdaje: 2011
ID: 1728599