Niko Rozman (Avtor), Tonica Bončina (Avtor), Ivan Anžel (Avtor), Franc Zupanič (Avtor)

Povzetek

In ternary Al-Mn-Be alloys a metastable quasicrystalline phase can form at relatively low cooling rates (≈ 100 K/s); however, besides the quasicrystalline phase other phases can also be present. We found that the investigated alloy is very prone to the formation of metastable phases, which are also quasicrystalline. Using different investigation methods we determined the type of phases, their shape, morphology, chemical composition and distribution. Special attention was given to the micro- and nano-sized quasicrystalline particles. When using slow cooling, Al10Mn3 and Be4AlMn were present; however, with a faster cooling rate a quasicrystal approximant and a quasicrystalline phase were formed.

Ključne besede

aluminium;quasicrystals;cooling rate;microstructure;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: Inštitut za kovinske materiale in tehnologije Ljubljana
UDK: 620.715:620.18
COBISS: 675242 Povezava se bo odprla v novem oknu
ISSN: 1580-2949
Matična publikacija: Materiali in tehnologije
Št. ogledov: 1016
Št. prenosov: 55
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni naslov: Vpliv ohlajevalne hitrosti na mikrostrukturo zlitine Al-Mn-Be
Sekundarni povzetek: V ternarnem zlitinskem sistemu Al-Mn-Be lahko nastane metastabilna kvazikristalna faza pri relativno majhni ohlajevalni hitrosti (≈ 100 K/s), vendar lahko poleg nje nastanejo še druge kristalne faze (predvsem intermetalne faze). Z uporabo različnih raziskovalnih metod smo ugotovili vrsto nastalih faz, kemijsko sestavo in porazdelitev. Ugotovili smo, da je zlitina nagnjena k nastanku metastabilnih faz (tudi kvazikristalnih). Predvsem so zanimivi kvazikristalni delci, ki se pojavljajo v mikro- in nanometrskih velikostih. S počasnim ohlajanjem so nastale faze Al10Mn3 in Be4AlMn, pri hitrem ohlajanju pa so se namesto njih pojavili kvazikristalni aproksimanti in kvazikristalne faze.
Sekundarne ključne besede: aluminij;kvazikristali;ohlajevalna hitrost;mikrostruktura;
URN: URN:NBN:SI
Vrsta dela (COBISS): Znanstveno delo
Strani: str. 65-68
Letnik: ǂVol. ǂ42
Zvezek: ǂno. ǂ2
Čas izdaje: 2008
ID: 1736692