Danilo Rojko (Avtor), Tomaž Vuherer (Avtor), Vladimir Gliha (Avtor)

Povzetek

Pri tem delu smo eksperimentalno analizirali posledice trdnostne neenakosti "over-matched" zvarnega spoja in položaja konice na vedenje pri lomu. Zvarni spoj je bil izdelan z varjenjen pod praškom (EPP). Primerjali smo lomno žilavost CTOD, določeno pri standardnih upogibnih (SENB) in velikih (WP) preizkušancih ter ocenili vpliv "constraint"-a pri nizkih temperaturah. Pri obeh tipih preizkušancev je bila razpoka narejena z utrujanjem materiala. Konica razpoke je bila v varu in grobozrnatem toplotno vplivanem področju (GZTVP). Lomno žilavost CTOD smo določali na podlagi predpisov, ki jih podaja BS 7448. oz. smernic raziskovalnega centra GKSS.

Ključne besede

varjenje;zvarni spoji;lomna žilavost;CTOD;konstrukcijsko jeklo;trdnostna neenakost;lokalna krhka področja;upogibni SENB preizkušanec;velik natezni WP preizkušanec;var;grobozrnato toplotno vplivano področje;utrujenostna razpoka;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: Inštitut za kovinske materiale in tehnologije Ljubljana
UDK: 621.791.052:539.55:669.14.018.298
COBISS: 6214166 Povezava se bo odprla v novem oknu
ISSN: 1580-2949
Matična publikacija: Materiali in tehnologije
Št. ogledov: 1907
Št. prenosov: 100
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Fracture toughness of over-matched weld joint measured on large and small scale specimens
Sekundarni povzetek: The effects of weld joint strength mismatiching and the crack tip position on the fracture behaviour of overmatched welded joints produced by submerged arc welding (SAW) have been experimentally analyzed. The comparison of CTOD fracture toughness values, determined on standard three-point bend speciments (SENB) and large scale tensile (WP) specimens, and the evaluation of the influence of constraint at loww temperatures has been made. In both types of specimen the crack was made by fatigue. The crack tip was located in the weld metal and the coarse grained heat affected zone. Fracture toughness values were calculated according to BS 7448 using the direct measuring method, developed at the GKSS Research Centre in Geesthacht.
Sekundarne ključne besede: welding;welded joints;fracture toughness;CTOD;constructional steel;strength mismatching;local brittle zones;three-point bend specimens;large-scale tensile speciments;weld metal;coarse grained heat affected zone;fatigue crack;