MIha Logar (Avtor), Milan Bizjak (Mentor)

Povzetek

V okviru diplomskega dela smo obravnavali problematiko nastanka poškodb pri hladnem preoblikovanju jeklene pločevine. Ker je pri teh postopkih stopnja deformacije lahko zelo visoka, se lahko na izdelkih pojavijo napake in poškodbe. V analizo smo vzeli šest trakov jeklene pločevine različnih šarž ter analizirali in naredili pregled s področja napak pri preoblikovanju nerjavne pločevine, z namenom iskanja razlogov za nastanek napak, ki se pojavljajo med preoblikovanjem določene šarže. Za nastanek napak v jeklu je možnih veliko razlogov, ki so povezani z orodjem, materialom ali vodenjem postopka preoblikovanja (npr. prevelika stopnja deformacije). Ker so se napake pojavile le na določenih trakovih, pri uporabi enakega orodja in deformacije, smo se v okviru diplomskega dela osredotočili na karakterizacijo jeklenih pločevin. Z analizo smo podrobneje karakterizirali vse lastnosti jekla, ki pomembno vplivajo na napovedovanje poteka preoblikovanja kot so mehanske lastnosti, kemijska sestava in mikrostruktura.

Ključne besede

nastanek poškodb;globoki vlek;anizotropija;mehanske lastnosti;karakterizacija jekel;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL NTF - Naravoslovnotehniška fakulteta
Založnik: [M. Logar]
UDK: 669
COBISS: 160028419 Povezava se bo odprla v novem oknu
Št. ogledov: 50
Št. prenosov: 1
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: damage development during cold forming of sheet forming
Sekundarni povzetek: The paper dealt with the problem of damage formation during cold forming of steel sheets. Since the deformation rate in these processes can be very high, defects and damage to the products can occur. Six steel sheet strips from different batches were examined and a survey of the range of defects in stainless steel sheet forming was made to determine the causes of the defects occurring in the forming of a particular batch. There are many possible reasons for the occurrence of defects in steel related to the tool, the material or the control of the forming process (e.g. too high strain rate). Since the defects occurred only on specific strips with the same tool and deformation, the focus of the work was on characterising the steels. The analysis was used to characterise in detail all the properties of the steel that have a significant influence on the prediction of the forming process, such as the mechanical properties, the chemical composition and the microstructure.
Sekundarne ključne besede: forming damage;deep drawing;anisotropy;mechanical properties;characterization of steels;
Vrsta dela (COBISS): Diplomsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Naravoslovnotehniška fak., Oddelek za materiale in metalurgijo
Strani: XIII, 56 f.
ID: 19271489