zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Luka Gašperšič (Avtor), Lidija Slemenik Perše (Mentor)

Povzetek

Jadralne deske so večinoma narejene iz polimerne pene, obdane s polimernimi kompozitnimi laminati. Za izdelavo kompozitnih laminatov pri jadralnih deskah se večinoma uporabljajo steklena vlakna ter epoksi smola. Epoksi smole, namenjene izdelavi jadralnih desk, so lahko tudi nekajkrat dražje kot epoksi smole, namenjene izdelavi klasičnih kompozitov. V okviru zaključne naloge je bila izvedena analiza razlik med takima smolama, z namenom optimizacije proizvodnih stroškov jadralnih desk. Izvedena je bila termična (DSC), reološka in mehanska (DMA) analiza obeh komercialno dostopnih epoksi smol. Ugotovljeno je bilo, da se smola, namenjena izdelavi jadralnih desk, v večini primerov zamreži hitreje kot smola, namenjena izdelavi klasičnih kompozitov. Zanimivo je, da smola, namenjena izdelavi klasičnih kompozitov, v veliko primerih po končanem procesu zamreževanja dosega višje vrednosti elastičnega in viskoznega modula kot smola, namenjena izdelavi jadralnih desk. Pri mehanski analizi ni prišlo do večjih razlik med smolama, ki sta bili zamreženi na sobni temperaturi.

Ključne besede

diplomske naloge;kompoziti;jadralna deska;epoksi smola;izdelava jadralnih desk;termične lastnosti termosetov;viskoelastične lastnosti;dinamična mehanska analiza;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [L. Gašperšič]
UDK: 678.686:677.521:797.148(043.2)
COBISS: 156214019 Povezava se bo odprla v novem oknu
Št. ogledov: 330
Št. prenosov: 52
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Analysis of epoxy resins, used in surfboard production
Sekundarni povzetek: Surfboards are mostly made of polymer foam encased in polymer composite laminates. Glass fibers and epoxy resin are commonly used for manufacturing composite laminates in surfboards. Epoxy resins, recommended for surfboard production can be several times more expensive than epoxy resins used for traditional composites. As part of this thesis, an analysis of two commercially available resins was performed with the aim of optimizing the production costs of surfboards. Thermal (DSC), rheological, and mechanical (DMA) analyses were performed on both materials. The results showed that the resin, recommended for surfboard production generally cures faster than the resin, used for traditional composites. Interestingly, the resin for traditional composites often reaches higher values of elastic and viscous modulus after curing compared to the resin for surfboard production. Moreover, there were no significant differences observed in mechanical properties of the two resins.
Sekundarne ključne besede: thesis;composites;surfboard;epoxy resin;surfboard production;thermal properties of thermosets;viscoelastic properties;dynamic mechanical analysis;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIII, 36 f.
ID: 19304477
Priporočena dela:
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, magistrsko delo