diplomsko delo
Povzetek
Postavili smo si vprašanje, ali orientacija vzorčenja vpliva na preoblikovalne lastnosti jekla. Zato smo se odločili, da bomo izvedli enostopenjske tlačne preizkuse na nerjavnem jeklu 316L. Preizkuse smo opravljali na termomehanskem simulatorju Gleeble 1500D. Opravili smo 16 preizkusov pri 4 različnih temperaturah (900 °C, 1000 °C, 1100 °C in 1200 °C) in pri dveh različnih hitrostih (0,1 s–1 in 1 s–1). Osem preizkušancev smo odvzeli prečno na smer valjanja, drugih osem pa vzdolž smeri valjanja. S pomočjo simulatorja Gleeble 1500D smo v računalniškem programu Origin izrisali krivulje tečenja in jih primerjali med seboj. Preizkušance smo nato opazovali s svetlobnim mikroskopom Zeiss AxioCam MRc5 in z računalniškim programom Axio Vision SE64 zajeli slike mikrostruktur.
Ključne besede
jeklo 316L;anizotropija;krivulja tečenja;nerjavna jekla;mikroskopija.;
Podatki
Jezik: |
Slovenski jezik |
Leto izida: |
2023 |
Tipologija: |
2.11 - Diplomsko delo |
Organizacija: |
UL NTF - Naravoslovnotehniška fakulteta |
Založnik: |
[M. Blagojević] |
UDK: |
669 |
COBISS: |
160157955
|
Št. ogledov: |
40 |
Št. prenosov: |
6 |
Ocena: |
0 (0 glasov) |
Metapodatki: |
|
Ostali podatki
Sekundarni jezik: |
Angleški jezik |
Sekundarni naslov: |
influence of sampling orientation on hot flow curves of AISI 316L stainless steel |
Sekundarni povzetek: |
We asked ourselves whether the orientation of the sampling affects the deformation characteristics of the steel. Therefore, we decided to perform single-stage pressure tests on 316L stainless steel. We performed the tests on the Gleeble 1500D thermomechanical simulator. We performed 16 tests at 4 different temperatures (900 °C, 1000 °C, 1100 °C in 1200 °C) and at two different speeds (0.1 s-1 and 1 s-1). Eight test subjects were taken transverse to the rolling direction and the other eight along the rolling direction. With the help of the Gleeble 1500D simulator, we plotted the flow curves on the Origin computer program and compared them with each other. Our test subjects were then observed on a Zeiss AxioCam MRc5 microscope and images of the microstructures were captured using the Axio Vision SE64 computer program. |
Sekundarne ključne besede: |
stainless steel 316L;anisotropy;flow curve;stainless steel;microscopy.; |
Vrsta dela (COBISS): |
Diplomsko delo/naloga |
Študijski program: |
0 |
Konec prepovedi (OpenAIRE): |
1970-01-01 |
Komentar na gradivo: |
Univ. v Ljubljani, Naravoslovnotehniška fak., Oddelek za materiale in metalurgijo |
Strani: |
X, 31 f. |
ID: |
19384828 |