diplomsko delo
Danilo Ščernjavič (Avtor), Jože Resnik (Recenzent), Milan Šernek (Mentor)

Povzetek

Raziskovali smo mehanske lastnosti različnih lesnih vrst in iz njih izdelanih kompozitov, ter možnost njihove uporabe v konstrukcijske namene. Uporabili smo 2 vrsti lepila in lesne vrste: bukev, smreko, macesen, lipo, brezo in jelšo. Lesove smo med sabo kombinirali v različne sestave lesnih kompozitov in jih nato lepili po vročem ali hladnem postopku. Iz teh lepljencev smo izdelali preskušance za ugotavljanje mehanskih lastnosti, vlažnosti in gostote. Po lepljenju smo izmerili in izračunali tudi izgubo debeline. Preizkus mehanskih lastnosti smo izvajali s pomočjo univerzalnega testirnega stroja Zwick Z100 po standardu SIST EN 310. Gostoto smo merili po standardu SIST EN 323, vlažnost pa po standardu SIST EN 322. Ugotovili smo, da so mehanske lastnosti lesnih kompozitov boljše kot mehanske lastnosti samega masivnega lesa. Prav tako pa imajo lesni kompoziti, zlepljeni po vročem postopku, boljše mehanske lastnosti od lesnih kompozitov, zlepljenih po hladnem postopku. Pri merjenju vlažnosti smo ugotovili, da ni bilo bistvenih razlik med masivnim lesom in lesnimi kompoziti Ugotovili smo tudi, da z lepljenjem lesa povečamo gostoto preskušancev. Lesni kompoziti, zlepljeni po vročem postopku, so imeli največjo, masiven les pa najmanjšo, gostoto.

Ključne besede

les;kompoziti;lepljenje;mehanske lastnosti;

Podatki

Jezik: Slovenski jezik
Leto izida:
Izvor: Ljubljana
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL BF - Biotehniška fakulteta
Založnik: [D. Ščernjavič]
UDK: 624.011
COBISS: 1646985 Povezava se bo odprla v novem oknu
Št. ogledov: 2759
Št. prenosov: 310
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Glued wood for construction purposes
Sekundarni povzetek: Mechanical properties of various wood species and glued composites, so as their applicability in construction purposes, were researched. Various test samples, prepared from different wood species (beech, pine, larch, lime, birch, alder), were glued in combinations using hot and cold gluing procedure. Combined samples were tested for mechanical properties, their moisture and density. After pressing, thickness loss was measured and calculated. Mechanical test was performed with Zwick Z100 machine according tostandard SIST EN 310; density according to standard SIST EN 323, and moisture according to standard SIST EN 322 were also measured. It was discovered that glued wood has better mechanical properties than massive wood,and also that samples made by hot gluing have better mechanical properties than those made by cold gluing. By measuring moisture it was proved that there was no essential difference between glued and massive wood. By density calculation it was found out that by gluing different species of wood the density of samples increases. Wooden composites made by hot gluing have greater density than massive wood.
Sekundarne ključne besede: wood;composites;gluing;mechanical properties;
Vrsta dela (COBISS): Diplomsko delo
Komentar na gradivo: Diplomsko delo, Univ. v Ljubljani, Biotehniška fak., Oddelek za lesarstvo
Strani: X, 67 f., [19 f. pril.]
Ključne besede (UDK): applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;engineering;technology in general;inženirstvo;tehnologija na splošno;civil and structural engineering in general;gradbena tehnika;gradbeništvo;structures and structural parts according to material and method of construction;nosilne konstrukcije in deli nosilne konstrukcije po gradivu [materialu] in načinu gradnje;
ID: 21390
Priporočena dela:
, ni podatka o podnaslovu
, diplomsko delo univerzitetnega študijskega programa