Žiga Jelen (Avtor), Marcin Krajewski (Avtor), Franc Zupanič (Avtor), Peter Majerič (Avtor), Tilen Švarc (Avtor), Ivan Anžel (Avtor), Jernej Ekar (Avtor), Sz-Chian Liou (Avtor), Jerzy Kubacki (Avtor), Mateusz Tokarczyk (Avtor), Rebeka Rudolf (Avtor)

Povzetek

A coupled process of ultrasonic spray pyrolysis and lyophilisation was used for the synthesis of dried gold nanoparticles. Two methods were applied for determining their melting temperature: uniaxial microcompression and differential scanning calorimetry (DSC) analysis. Uniaxial microcompression resulted in sintering of the dried gold nanoparticles at room temperature with an activation energy of 26–32.5 J/g, which made it impossible to evaluate their melting point. Using DSC, the melting point of the dried gold nanoparticles was measured to be around 1064.3°C, which is close to pure gold. The reason for the absence of a melting point depression in dried gold nanoparticles was their exothermic sintering between 712 and 908.1°C.

Ključne besede

zlati nanodelci;tališče;ultrazvočna razpršilna piroliza;karakterizacija;gold nanoparticles;melting point;ultrasonic spray pyrolysis;characterisation;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: De Gruyter
UDK: 669.2/.8:620.3
COBISS: 158645507 Povezava se bo odprla v novem oknu
ISSN: 2191-9097
Št. ogledov: 224
Št. prenosov: 12
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: zlati nanodelci;tališče;ultrazvočna razpršilna piroliza;karakterizacija;
Vrsta dela (COBISS): Članek v reviji
Strani: 12 str.
Letnik: ǂVol. ǂ12
Zvezek: ǂiss. ǂ1
Čas izdaje: July 2023
DOI: 10.1515/ntrev-2022-0568
ID: 21548171