In-situ micro-asperity investigation of real contact area formation during sliding with the effects of roughness and normal load considered

Petra Jan (Avtor), Blaž Brodnik Žugelj (Avtor), Mitjan Kalin (Avtor)

Povzetek

Real contact area is a challenging phenomenon in tribology, where despite established theoretical models, detailed experimental studies are still lacking. This work is focused on the evolution of the real contact area of multi-asperity steel contacts during sliding, by using sub-micron characterisation of entire multi-asperity contact area and simultaneous measurement of the friction force. Steel-sapphire contact was monitored by using an in-situ optical system in real time during 5 mm of unidirectional sliding in surface roughness range R$_a$ = 0.1–1.0 µm and normal loads up to the nominal contact pressure equal to steel yield strength (Y). The results showed that the initial real contact area caused by static loading increased during sliding. At low nominal contact pressure of 0.3Y, the increase in real contact area was the largest: for R$_a$ = 0.1 µm it went from 9.5% of the nominal area under static conditions to 15.0% after sliding, a 56% relative increase, and for R$_a$ = 1.0 µm it went from 5.0% to 11.5% after sliding, a 106% increase. The increase in real contact area was smaller at higher nominal contact pressures of 0.6Y and 1.0Y. At 1.0Y for R$_a$ = 0.1 µm the real contact area went from 18.0% to 21.8% after sliding and for R$_a$ = 1.0 µm it went from 9.4% to 12.9% after sliding. The coefficient of friction increased with roughness at the lowest nominal contact pressure 0.3Y (for R$_a$ = 0.1 µm it was 0.24 and for R$_a$ = 1.0 µm it was 0.29) but became independent of roughness at higher contact pressures (on average 0.18).

Ključne besede

realna kontaktna površina;drsni kontakt;realistične inženirske površine;in-situ meritev v realnem času;real contact area;sliding contact;realistic engineering surfaces;real-time in-situ measurement;

Podatki

Jezik:	Angleški jezik
Leto izida:	2024
Tipologija:	1.01 - Izvirni znanstveni članek
Organizacija:	UL FS - Fakulteta za strojništvo
UDK:	539.92
COBISS:	176779779
ISSN:	1879-2464
Št. ogledov:	179
Št. prenosov:	21
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Slovenski jezik
Sekundarne ključne besede:	realna kontaktna površina;drsni kontakt;realistične inženirske površine;in-situ meritev v realnem času;
Vrsta dela (COBISS):	Članek v reviji
Strani:	str. 1-9
Zvezek:	ǂVol. ǂ191
Čas izdaje:	Mar. 2024
DOI:	10.1016/j.triboint.2023.109171
ID:	21627728