Tilen Švarc (Avtor), Matej Zadravec (Avtor), Žiga Jelen (Avtor), Peter Majerič (Avtor), Blaž Kamenik (Avtor), Rebeka Rudolf (Avtor)

Povzetek

This study demonstrates the successful synthesis of Ni/Y2O3 nanocomposite particles through the application of ultrasound-assisted precipitation using the ultrasonic spray pyrolysis technique. They were collected in a water suspension with polyvinylpyrrolidone (PVP) as the stabiliser. The presence of the Y2O3 core and Ni shell was confirmed with transmission electron microscopy (TEM) and with electron diffraction. The TEM observations revealed the formation of round particles with an average diameter of 466 nm, while the lattice parameter on the Ni particle’s surface was measured to be 0.343 nm. The Ni/Y2O3 nanocomposite particle suspensions were lyophilized, to obtain a dried material that was suitable for embedding into a polylactic acid (PLA) matrix. The resulting PLA/Ni/Y2O3 composite material was extruded, and the injection was moulded successfully. Flexural testing of PLA/Ni/Y2O3 showed a slight average decrease (8.55%) in flexural strength and a small decrease from 3.7 to 3.3% strain at the break, when compared to the base PLA. These findings demonstrate the potential for utilising Ni/Y2O3 nanocomposite particles in injection moulding applications and warrant further exploration of their properties and new applications in various fields.

Ključne besede

ultrazvočna razpršilna piroliza;liofilizacija;sušenje z zamrzovanjem;ekstrudiranje;injekcijsko brizganje;ultrasound spray pyrolysis;Ni/Y2O3;lyophilization;PLA;extrusion;injection moulding;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: MDPI
UDK: 669.2:536
COBISS: 160771075 Povezava se bo odprla v novem oknu
ISSN: 1996-1944
Št. ogledov: 8
Št. prenosov: 0
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarne ključne besede: ultrazvočna razpršilna piroliza;liofilizacija;sušenje z zamrzovanjem;ekstrudiranje;injekcijsko brizganje;
Vrsta dela (COBISS): Članek v reviji
Strani: 15 str.
Letnik: ǂVol. ǂ16
Zvezek: ǂiss. ǂ14, [article no.] 5162
Čas izdaje: July 2023
DOI: 10.3390/ma16145162
ID: 23349921