magistrsko delo
Samo Stankovič (Avtor), Aleš Podgornik (Mentor), Marjan Marinšek (Član komisije za zagovor), Boštjan Genorio (Član komisije za zagovor)

Povzetek

V delu je bila izvedena hidrotermalna sinteza SnO2 delcev pri različnih procesnih parametrih. Večinski del magistrske naloge je bil posvečen analizi morfologije prekurzorja v procesu (Na$_2$[Sn(OH)$_6$]) oziroma odvisnosti morfologije prekurzorja od pogojev sinteze, čemur so bile posvečene tri hipoteze, četrta pa se je nanašala na vpliv hidrotermalnih pogojev na nastanek končnega produkta. Nastanek SnO$_2$ je bil potrjen na podlagi topnosti končnega produkta in ujemanja z obstoječo literaturo; posnete so bile tudi SEM slike. Morfološke značilnosti prekurzorja so bile analizirane s pomočjo optičnega mikroskopa. Preverjen je bil širok razpon pogojev za sintezo, podlagi česar so bile prve tri hipoteze potrjene – zelo jasno je razvidno, da lahko že majhne razlike v parametrih povzročijo precejšnje morfološko odstopanje. Hipoteza številka štiri je bila ovržena, saj je bilo pokazano, da se pri izbranih pogojih morfologija prekurzorja ne ohranja pri končnem produktu.

Ključne besede

hidrotermalna sinteza;kositrov dioksid;natrijev heksahidroksidostanat(IV);morfologija;magistrska dela;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [S. Stankovič]
UDK: 66.091.3:546.811-31(043.2)
COBISS: 207438851 Povezava se bo odprla v novem oknu
Št. ogledov: 35
Št. prenosov: 20
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Hydrothermal synthesis and characterisation of SnO$_2$ particles
Sekundarni povzetek: In the work, the hydrothermal synthesis of SnO2 particles was carried out at different process parameters. The major part of the master's thesis was devoted to the analysis of the morphology of the precursor in the process (Na$_2$[Sn(OH)$_6$]) or the dependence of the morphology of the precursor on the synthesis conditions, to which three hypotheses were devoted, while the fourth related to the influence of hydrothermal conditions on the formation of the final product. The formation of SnO$_2$ was confirmed based on the solubility of the final product and agreement with existing literature; SEM images were also taken. The morphological characteristics of the precursor were analyzed using an optical microscope. A wide range of synthesis conditions were tested, on the basis of which the first three hypotheses were confirmed - it is very clear that even small differences in parameters can lead to a significant morphological deviation. Hypothesis number four was disproved, as it was shown that under the selected conditions the morphology of the precursor is not preserved in the final product.
Sekundarne ključne besede: hydrothermal synthesis;tin(IV) oxide;sodium hexahydroxostannate(IV);morphology;Anorganska sinteza (kemija);Kasiterit;Univerzitetna in visokošolska dela;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 1000376
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za kemijo in kemijsko tehnologijo, smer Kemijsko inženirstvo
Strani: 1 spletni vir (1 datoteka PDF (88 str.))
ID: 24956297