Mahadevan Govindasamy (Avtor), Lloyd Jenner Joseph Manuel Mangalakaran (Avtor), Senthilkumar Thamilkolunthu (Avtor)

Povzetek

The corrosion behavior of dissimilar weldments between AISI310 and AISI2205 stainless steels in a 5 % calcium chloride solution at 50 °C was investigated under three conditions: as-welded, lower post-weld heat treatment at 800 °C, and higher post-weld heat treatment at 1000 °C. Microstructural examination revealed severe pitting in the as-welded sample, with pit widths ranging from 270 μm to 360 μm. The lower heat-treated sample had larger pits (310 μm to 370 μm), while the higher heat-treated sample showed homogeneous corrosion with a protective oxide coating. The as-welded sample had the highest corrosion rate, followed by the lower heat-treated sample, which had a moderate rate, and the higher heat-treated sample had the lowest rate. The corrosion current densities were 5,26 × ▫$10^{-3}$▫ mA/cm², 4,6 × ▫$10^{-4}$▫ mA/cm² and 1,4 × ▫$10^{-4}$▫ mA/cm², respectively. Electrochemical noise measurements confirmed these findings, with the higher heat-treated sample showing negligible localized corrosion and homogenous corrosion behavior.

Ključne besede

AISI2205;corrosion;electrochemical impedance spectroscopy;Ca▫$Cl_2$▫;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UL FS - Fakulteta za strojništvo
UDK: 621
COBISS: 227927811 Povezava se bo odprla v novem oknu
ISSN: 2536-3948
Št. ogledov: 22
Št. prenosov: 0
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Slovenski jezik
Sekundarni povzetek: Korozijsko obnašanje neenakih zvarov nerjavnih jekel AISI310 in AISI2205v 5-odstotni raztopini kalcijevega klorida pri 50 °C je bilo raziskano pod tremi pogoji: kot varjeno, z nižjo toplotno obdelavo po varjenju pri 800 °C in z višjo toplotno obdelavo po varjenju pri 1000 °C. Mikrostrukturna analiza je pokazala izrazito jamasto korozijopri varjenem vzorcu, pri čemer so bile širine jamic med 270 μm in 360 μm. Vzorec z nižjo toplotno obdelavo je imel večje vdolbine (310 μm do 370 μm), medtem ko je pri vzorcu, ki je bil toplotno obdelan višje, opaziti homogeno korozijo z zaščitno oksidno prevleko. Najvišjo stopnjo korozije je imel varjeni vzorec, sledil mu je nizko- toplotno obdelani vzorec z zmerno stopnjo, najnižjo stopnjo korozije pa je imel visoko-toplotno obdelani vzorec. Gostote korozijskega toka so bile 5,26 × ▫$10^{-3}$▫ mA/cm², 4,6 × ▫$10^{-4}$▫ mA/cm² oziroma 1,4 × ▫$10^{-4}$▫ mA/cm². Elektrokemične meritve šuma so potrdile te ugotovitve, pri čemer je vzorec, ki je bil obdelan z višjo toplotno obdelavo, pokazal zanemarljivo lokalizirano korozijo in homogeno korozijsko obnašanje.
Strani: str. 3-9
Letnik: ǂVol. ǂ71
Zvezek: ǂno. ǂ1/2
Čas izdaje: 2025
DOI: 10.5545/sv-jme.2024.1084
ID: 26010936