Jožef Klepec (Avtor), Violeta Bokan-Bosiljkov (Mentor), Tomo Cerovšek (Član komisije za zagovor), Boštjan Brank (Član komisije za zagovor), Andraž Hočevar (Komentor)

Povzetek

Vpliv vodocementnega razmerja in količine superplastifikatorja na reološke lastnosti svežih cementnih malt

Ključne besede

gradbeništvo;diplomska dela;VSŠ;sveža cementna malta;cementni kompoziti;razlez;reologija svežih cementnih malt;vodocementno razmerje;superplastifikator;

Podatki

Jezik: Slovenski jezik
Leto izida:
Izvor: Ljubljana
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FGG - Fakulteta za gradbeništvo in geodezijo
Založnik: [J. Klepec]
UDK: 691.3.001.41(043.2)
COBISS: 6245729 Povezava se bo odprla v novem oknu
Št. ogledov: 2357
Št. prenosov: 701
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Influence of water-to-cement ratio and superplasticizer content on rheological properties of fresh cement mortars
Sekundarni povzetek: In framework of this thesis we carried out tests on fresh cement mortars. The main purpose was to find out how the water-to-cement ratio and superplasticizer content determine rheological characteristics of fresh cement mortar. With the use of the CEM method we designed four reference mortar mixtures, based on the composition of concretes that had already been determined and analyzed in some other thesis. Additional mixtures were then made by modifying the reference mortars, composition in such way that the content of water or superplasticizer was varied. All mixtures were made of aggregate, cement, water and admixtures. As admixtures we used superplasticizer and air entraining agent. We also used two different types of cement. The tests were carried out using standard method of flow table tests for fresh mortars and non-standard measurement of rheological properties by using rheometer ConTec Viscometer 5. The main emphasis of the research work was on rheological measurements and the appertaining analyses of the obtained rheological parameters. Based on the analyses carried out we were able to confirm the findings from literature about the influence of water-to-cement ratio and superplasticizer content on rheological properties of fresh cement mortars. Finally, rheological parameters were compared with the results of flow table tests.
Sekundarne ključne besede: graduation thesis;civil engineering;fresh cement mortar;cement composities;rheology of fresh cement mortars;water-to-cement ratio;superplasticizer;
Vrsta datoteke: application/pdf
Vrsta dela (COBISS): Diplomsko delo
Komentar na gradivo: Univ. v Ljubljani, Fak. za gradbeništvo in geodezijo
Strani: XII, 63 str.
Ključne besede (UDK): applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;building (construction) trade;building materials;building practice and procedure;gradbeništvo;gradbeni materiali;gradbene obrti in dela;building materials;building components;gradiva;gradbeni [konstrukcijski] deli;
ID: 29332
Priporočena dela:
, diplomsko delo visokošolsko strokovnega študijskega programa
, diplomsko delo visokošolskega študija gradbeništva
, diplomsko delo univerzitetnega študijskega programa