diplomska naloga
Dora Kovač (Avtor), Violeta Bokan-Bosiljkov (Mentor), Janko Logar (Član komisije za zagovor), Andreja Padovnik (Komentor)

Povzetek

V sklopu diplomskega dela sem ugotavljala vpliv različnih dodatkov na lastnosti apnenih injekcijskih mešanic za restavriranje arhitekturnih površin objektov kulturne dediščine. Veliki del naloge je bil praktičnega tipa in je potekal v laboratoriju Fakultete za gradbeništvo in geodezijo Univerze v Ljubljani. V laboratoriju smo oblikovali mešanice na osnovi hidratiziranega apna in kalcitne moke z dodatki superplastifikatorja, amonijevega karbamata, tufa (naravnega pucolana) in ultralahkih polnil. S pomočjo standardiziranih metod smo na svežih vzorcih določali: prostorninsko maso sveže mešanice, pretočnost, izločanje vode in vodozadržnost. Na strjenih vzorcih smo naredili standardizirane preiskave upogibne in tlačne trdnosti ter nestandardizirano preiskavo krčenja. Na podlagi opravljenih predhodnih preiskav smo izbrali najboljše mešanice, za katere smo določali tudi sposobnost injektiranja. V prvem delu naloge sem predstavila problematiko odstopanja ometov od površine na objektih kulturne dediščine, izvedbo laboratorijskih preiskav in kriterije, ki jih je potrebno izpolniti pri zasnovi injekcijskih mešanic. Drugi del naloge je namenjen analiziranju rezultatov opravljenih preiskav in primerjavi le teh med seboj.

Ključne besede

gradbeništvo;diplomska dela;UNI;B-GR;apnene injekcijske mešanice;kemijski dodatki;superplastifikator;mineralni dodatki;ultralahko polnilo;predhodne preiskave;sposobnost injektiranja;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FGG - Fakulteta za gradbeništvo in geodezijo
Založnik: [D. Kovač]
UDK: 691.53(043.2)
COBISS: 6835809 Povezava se bo odprla v novem oknu
Št. ogledov: 1464
Št. prenosov: 468
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Effect of binding acceletarors and lightweight aggregate fillers on the performance characteristics of lime-based injection grouts
Sekundarni povzetek: The aim of my thesis was to determine the effect of different admixtures on the performance characteristics of lime-based injection grouts for restoration of architectural surfaces. A large part of my thesis was practically orientated and was carried out in the laboratory of the Faculty of Civil and Geodetic Engineering of University of Ljubljana. In the laboratory we developed lime-based injection grouts with additives like superplasticizer, ammonium carbamate, tuff (natural pozzolan) and lightweight aggregate filler. By standardized test methods we first determined properties of grouts in fresh state: wet density, flow value, expansion and bleeding, water retention and water release. On samples in hardened state standardized tests to determine flexural and compressive strength were carried out, along with non-standardized test of shrinkage. Once the results of preliminary tests had been obtained, we choose the best grouts for the test of injectability. In the first part of my thesis I presented the problems of degradation and delamination of architectural surfaces of cultural heritage buildings, description of laboratory tests and criteria that have to be fulfilled in the process of design of lime-based injection grouts. The second part is focused on analysis of test results and their comparison.
Sekundarne ključne besede: graduation thesis;civil engineering;lime-based injection grouts;chemical admixtures;superplasticizer;mineral additives;lightweight aggregate filler;preliminary tests;injectability test;
Vrsta datoteke: application/pdf
Vrsta dela (COBISS): Diplomsko delo/naloga
Komentar na gradivo: Univ. v Ljubljani, Fak. za gradbeništvo in geodezijo
Strani: XII, 34 str.
ID: 8708251