diplomska naloga
Nika Šubic (Avtor), Drago Saje (Mentor), Janko Logar (Član komisije za zagovor)

Povzetek

Beton visoke trdnosti se ponaša z mnogimi dobrimi lastnostmi a ima tudi negativne, kot je na primer veliko avtogeno krčenje. Le to lahko zmanjšamo z dodajanjem predhodno namočenega lahkega agregata v betonsko mešanico. V diplomski nalogi obravnavamo vpliv različnih lahkih agregatov na tlačne trdnosti in krčenje betona. Opisani so faktorji, od katerih je odvisna učinkovitost lahkega agregata kot notranjega rezervoarja vode. V eksperimentalnem delu diplomske naloge smo primerjali betonske mešanice, ki so vsebovale različni vrsti predhodno namočenega lahkega agregata. Uporabljen je bil naraven lahek agregat Lehnjak frakcij 0-2mm in 2-4mm ter ekspandirana glina Liapor enakih frakcij. Vse štiri betonske mešanice so vsebovale 12% lahkega agregata. Primerjali smo jih s kontrolno mešanico, ki je vsebovala le običajen agregat. Dodajanje predhodno namočenega lahkega agregata v betonsko mešanico se izkaže za ugodno, saj izboljša lastnosti betona. Opazna je tudi razlika med betonskimi mešanicami z dodano različno vrsto in različno zrnavostno strukturo lahkega agregata. Uporaba predhodno namočene ekspandirane gline frakcije 0-2mm, glede na primerljiv beton brez predhodno namočenega lahkega agregata, poveča tlačno trdnost betona in zmanjša njegovo krčenje.

Ključne besede

gradbeništvo;diplomska dela;UNI;B-GR;lahek agregat;notranja nega betona;betoni visoke trdnosti;avtogeno krčenje;krčenje zaradi sušenja;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FGG - Fakulteta za gradbeništvo in geodezijo
Založnik: [N. Šubic]
UDK: 624.012.4(497.4)(043.2)
COBISS: 6838625 Povezava se bo odprla v novem oknu
Št. ogledov: 2114
Št. prenosov: 747
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: ǂThe ǂimpact of different lightweight aggregates on properties of high strength concrete
Sekundarni povzetek: High strength concrete is known for its many favorable qualities. However it also has some negative characteristics like autogenous shrinkage which can be reduced by adding saturated lightweight aggregate to the concrete mix. The effect of using different types of lightweight aggregate on compressive strength and shrinkage of concrete is discussed in this graduation thesis. Factors influencing the success of internal curing with prewetted lightweight aggregate are described in theoretical part of the thesis and experiments using different kinds of lightweight aggregate were conducted in experimental part. Materials used were natural lightweight aggregate of fractions 0-2 and 2-4 and expanded clay of the same fractions. Four concrete mixes containing 12% of different lightweight aggregates were compared to a comparable concrete mix without lightweight aggregate. It appears that the use of prewetted lightweight aggregate improves the performance of high strength concrete; however the variation of results is noticeable. The type and grading of lightweight aggregate we add to the cement mix has an influence on the effectiveness of internal curing. In comparison with a similar concrete without prewetted lightweight aggregate, adding prewetted expanded clay of fraction 0-2mm increases compressive strength and decreases autogenous shrinkage of high strength concrete.
Sekundarne ključne besede: graduation thesis;civil engineering;lightweight aggregate;internal curing of concrete;high performance concretes;autogenous shrinkage;drying shrinkage;
Vrsta datoteke: application/pdf
Vrsta dela (COBISS): Diplomsko delo/naloga
Komentar na gradivo: Univ. v Ljubljani, Fak. za gradbeništvo in geodezijo
Strani: X, 32 str.
ID: 8708435