Vladimir Gliha (Avtor), Zijah Burzić (Avtor), Tomaž Vuherer (Avtor)

Povzetek

The fatigue strength of polycrystalline metals is hardness and defect size dependent. The fatigue strength of welds depends on the size of grains and actual local mean stress, too. Local mean stress is influenced by the global R-ratio and static preloading. The welds in the as-welded condition are pre-stressed due to the existence of welding residual stresses. The sign and magnitude of residual stresses depend on the welding conditions. Changes of residual stresses, hardness and defect size are experimentally determined in the present work. Samples of studied metals are prepared by using either thermal cycle simulator or laboratory furnace and water quenching. The methods of microstructure preparation and type of load result in actual local R-ratio at the used weld toe models. Specimens are cyclic loaded in the similar way as steel at the weld toe. The bottom of the notch is either defect-free or defected by Vickers indentation. Final results show that coarser grain and higher local R-ratios lower the fatigue strength of welds.

Ključne besede

CrNiMo steels;weld;fatigue resistance;heat-affected zone;small weld defects;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.08 - Objavljeni znanstveni prispevek na konferenci
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 621.791.05:539.431
COBISS: 14779670 Povezava se bo odprla v novem oknu
ISSN: 1451-3749
Št. ogledov: 1267
Št. prenosov: 21
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Neki faktori koji utiču na otpornost zavara prema zamoru
Sekundarne ključne besede: CrNiMo jekla;zvar;odpornost proti utrujanju;toplotno vplivano območje;majhne varilne napake;
URN: URN:SI:UM:
Strani: str. 239-244
Letnik: ǂVol. ǂ10
Zvezek: ǂbr. ǂ3
Čas izdaje: 2010
ID: 8718045