A Cu-Sn-Zn-Pb alloy was irradiated by ultraviolet nitrogen laser pulses (N2 laser, wave length 337 nm, pulse duration 6 ns, frequency 1 Hz, power 0.5 MW and average power density 0.67 GW/m2). The surface topography and microstructure were mainly studied by scanning electron microscopy, and a focused ion beam. The non-homogenized spatial beam profile resulted in the activation of several ablative mechanisms, the main being phase explosion and hydrodynamic instability. They caused a crater to be formed, surrounded by a raised rim and wavelike structure in a halo. FIB cross-sectioning and imaging showed a shallow (few micrometers) molten and resolidified surface layer. Streaks were observed in the heat-affected zone beneath the molten layer, indicating partial recrystallization of initially cold-worked material.

Ključne besede

preiskava materialov;mikrostruktura;topografija;bakrove zlitine;laser;fokusirani ionski snopi;ultravijolični dušikov laser;SEM;laserska ablacija;materials investigation;microstructure;topography;copper alloys;focused ion beams;UV nitrogen laser pulses;Scanning Electron Microscopy;laser ablation;

Podatki

Jezik: Angleški jezik
Leto izida:
Tipologija: 1.01 - Izvirni znanstveni članek
Organizacija: UM FS - Fakulteta za strojništvo
UDK: 620.18:[535.374:621.375.8]:669.35
COBISS: 11883798 Povezava se bo odprla v novem oknu
ISSN: 0925-8388
Št. ogledov: 1605
Št. prenosov: 124
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarne ključne besede: preiskava materialov;mikrostruktura;topografija;bakrove zlitine;laser;fokusirani ionski snopi;ultravijolični dušikov laser;SEM;laserska ablacija;
URN: URN:SI:UM:
Strani: str. 197-204
Letnik: ǂVol. ǂ465
Zvezek: ǂiss. ǂ1/2
Čas izdaje: oct. 2008
ID: 8718591