diplomsko delo
Lara Valentić (Avtor), Nataša Zabukovec Logar (Mentor)

Povzetek

V diplomskem delu sem želela raziskati razlike v sposobnostih za vezavo ogljikovega dioksida v kovinsko-organskih poroznih (MOF) materialih, sintetiziranih z okoljsko manj obremenjujočimi reaktanti, kot so trenutno v uporabi, in oceniti primernost materialov za zajem ogljikovega dioksida iz dimnih plinov v že obstoječih tehnoloških procesih. Pri sintezah sem spreminjala vir Mg in Al ionov, vrsto organskih ligandov in topil, temperaturo in čas sinteze. Večina produktov je bila narejena s solvotermalno sintezo, dva produkta sem poskusila optimizirati z mikrovalovno sintezo. Sintetiziranim produktom sem določala strukturo in/ali poroznost z uporabo rentgenske difrakcije (XRD), elektronske mikroskopije z uporabo elementne analize (SEM in EDX) ter s fizisorpcijo dušika. Najprimernejše produkte sem nato testirala za zajem ogljikovega dioksida. Najboljši produkt za zajemanje ogljikovega dioksida je Al-BPDC, aromatski kovinsko-organski porozni material z BET-specifično površino 1712 m2/g. Alifatski produkti z aluminijem in magnezijem (sukcionat, glutarat in pimelat) imajo opazno stopnjo adsorpcije šele pri visokih tlakih, zato niso primerni za adsorpcijo in zajem ogljikovega dioksida iz dimnih plinov.

Ključne besede

kovinsko-organski porozni materiali;zajem CO2;strukturna karakterizacija;alifatski karboksilati;aromatski karboksilati;diplomske naloge;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UNG FZO - Fakulteta za znanosti o okolju
Založnik: [L. Valentić]
UDK: 54
COBISS: 3998459 Povezava se bo odprla v novem oknu
Št. ogledov: 5397
Št. prenosov: 259
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Optimization of porous materials for CO2 capture
Sekundarni povzetek: In my diploma thesis, I wanted to study differences in capacity for carbon dioxide capture in metal-organic framework (MOF) materials, synthesized with environmentally more acceptable reagents that currently used ones. Furthermore, I did evaluation of synthesized products for carbon capture from gas mixtures in already existing technological processes. In the synthesis of products, I have changed the source of Al and Mg ions, type of organic ligands and solvents, temperature and time of synthesis. Majority of the products were synthesised with solvothermal synthesis, but I have also tried to optimize two products with microwave synthesis. All products were further analysed with X-Ray diffraction (XRD), electron microscopy (SEM), elemental analysis (EDX) and nitrogen physisorption to determine structure and/or porosity. Most appropriate products were chosen for testing the carbon dioxide adsorption. The best synthesised product for carbon capture is Al-BPDC, aromatic MOF-material with BET specific surface 1712 m2/g. Aluminium and magnesium aliphatic products with succinic, glutaric and pimelic acid have noticeable adsorption rates at high pressures, therefore they are not appropriate for carbon capture from flue gases.
Sekundarne ključne besede: Metal-organic framework materials;CO2 capture;structure characterization;aliphatic carboxylates;aromatic carboxylates;
URN: URN:SI:UNG
Vrsta dela (COBISS): Diplomsko delo/naloga
Komentar na gradivo: Univ. v Novi Gorici, Fak. za znanosti o okolju
Strani: IX, 52 str.
ID: 9063292