diplomsko delo
Vanja Spahič (Avtor), Lidija Fras Zemljič (Mentor), Simona Vajnhandl (Komentor)

Povzetek

Zaradi naraščanja svetovnega prebivalstva in posledično večje proizvodnje, uporabe in odlaganja polimernih materialov, je recikliranje le-teh postala nujnost . Polietilen tereftalat (PET) je v tekstilni industriji najbolj uporabljen sintetični material, kljub temu pa je recikliranje PET-a iz tekstilnih materialov manj raziskano področje. V diplomskem delu smo PET vlakna depolimerizirali s postopkom nevtralne hidrolize, stopnjo depolimerizacije pa določili s pomočjo titracij. Rezultati so pokazali, da se je PET najbolje razgradil pri temperaturi 250 oC, tlaku 39 barov, razmerju PET : voda 1:10 ter reakcijskem času 30 min. Titracije so se izkazale za primerno metodo za ocenitev stopnje razgradnje PET-a. Zaključki diplomske naloge so obetavni in odpirajo nove možnosti raziskav na področju titracij kot hitrih in enostavnih metod.

Ključne besede

depolimerizacija;polietilen tereftalat;PET;recikliranje;titracije;nevtralna hidroliza;diplomske naloge;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: [V. Spahič]
UDK: 678.095.268(043.2)
COBISS: 20426518 Povezava se bo odprla v novem oknu
Št. ogledov: 1249
Št. prenosov: 87
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Determination of the degree of depolymerisation of PET by means of titrations
Sekundarni povzetek: Due to the increasing world population and the resulting increased production, use and disposal of plastic materials and recycling them has become a necessity. Polyethylene terephthalate (PET) is in the textile industry the most used synthetic material, however, the recycling of PET textile materials is less researched area. In this thesis PET fibers were depolymerized with the procedure neutral hydrolysis and the rate of depolymerization was determined by titration. The results showed that PET was most degraded at a temperature of 250 °C, a pressure of 39 bar, a ratio of PET: water 1:10 and a reaction time of 30 min. Titration have proven to be an appropriate method to evaluate the degree of degradation of PET. The conclusions of the thesis are promising and opening up new possibilities for research in the field of titrations as quick and easy methods.
Sekundarne ključne besede: depolymerization;polyethylene terephtalate;recycling;neutral hydrolysis;titration;