Vpliv vrste veziva na lastnosti sanacijskih ometov

diplomska naloga

Mateja Vasić (Avtor), Violeta Bokan-Bosiljkov (Mentor), Petra Štukovnik (Komentor)

Povzetek

V sklopu diplomske naloge smo opravili preiskave na svežih in strjenih maltnih mešanicah, namenjenih izdelavi sanacijskih ometov. Glavni namen je bil pripraviti različne sestave malt za sanacijske omete, ki bodo dosegale čim večjo poroznost in paroprepustnost pri ustrezni tlačni trdnosti. Ugotoviti smo želeli, kako različna vrsta veziva in kemijski dodatki vplivajo na te lastnosti malt. V prvem delu diplomske naloge smo na podlagi izbranih razmerij med agregatom, vezivom in dodatki po več poizkusih dodajanja različnih količin vode dobili končne recepture mešanic. Kot kemijska dodatka smo uporabili superplastifikator in aerant, kot vezivo pa dve različni vrsti cementa in apno. Na svežih mešanicah smo raziskave opravili s standardizirano metodo določanja razleza na stresalni mizici ter določili prostorninsko maso malt in vsebnost por. V drugem delu smo na strjenih vzorcih starih 28 dni določili tlačno trdnost in merili difuzijo vodne pare. Vse rezultate, ki smo jih dobili s preiskavami, smo podali v preglednicah in na grafih.

Ključne besede

gradbeništvo;diplomska naloga;OG-MO;vrsta veziva;sanacijski ometi;razlez;prostorninska masa;vsebnost por;tlačna trdnost;difuzija vodne pare;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2016
Tipologija:	2.11 - Diplomsko delo
Organizacija:	UL FGG - Fakulteta za gradbeništvo in geodezijo
Založnik:	[M. Vasić]
UDK:	691:620.1(043.2)
COBISS:	7765089
Št. ogledov:	2219
Št. prenosov:	577
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Influence of binder type on the properties of restoration renders
Sekundarni povzetek:	As part of this thesis, a test was made on fresh and hardened mortar mixtures aimed at preparing restoration renders. The main purpose was to prepare various compositions of mortar for restoration renders that would have the highest possible air content and water vapour permeability at adequate compressive strength. We wanted to find out how different types of binders and chemical admixtures affect these properties of mortars. Based on the given ratio between the aggregate, the binder and the admixtures, the first part of the thesis focuses on the final mixture compositions that were obtained after several attempts of adding different amounts of water to them. Superplasticizer and air entraining agent were used as chemical admixtures and as binders two different types of cement and lime were used. Research on the fresh mixtures was conducted with standardized methods of determining the flow value on the flow table, after which the density and porosity of mortar were determined. In the second part of the thesis, compressive strength and water vapour diffusion were tested on 28-day-old hardened samples. All the results obtained during the tests are given in tables and graphs.
Sekundarne ključne besede:	type of binder;restoration plaster;flow value;density;porosity;compressive strength;water vapour diffusion;