diplomska naloga
Ina Vogel (Avtor), Andreja Goršek (Mentor), Darja Pečar (Komentor)

Povzetek

Preučevali smo korozijsko obnašanje nerjavnega jekla W. Nr. 1.4057 v raztopini H2SO4, s koncentracijo, c = 0.075 mol/L, ob dodatkih inhibitorjev različnih koncentracij. Uporabili smo štiri različne inhibitorje (Na3PO4, NaNO2, Na2O7Si3, Na2B4O7) in kombinacijo dveh (NaNO2/Na2B4O7). Poskuse smo opravili z gravimetrično metodo v skladu z ASTM G31 standardom. Določali smo izgubo mase, iz katere smo izračunali hitrost korozije in učinkovitost inhibitorjev. Opravili smo tudi elektrokemijske meritve, ob dodatku inhibitorja NaNO2 različnih koncentracij. Z analizo rezultatov smo ugotovili, da se z večanjem ustrezne koncentracije inhibitorja, zmanjša korozijski proces izbranega jekla.

Ključne besede

korozija;nerjavno jeklo;inhibitorji;gravimetrična metoda;hitrost korozije;učinkovitost inhibitorjev;

Podatki

Jezik: Slovenski jezik
Leto izida:
Izvor: Maribor
Tipologija: 2.11 - Diplomsko delo
Organizacija: UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [I. Vogel]
UDK: 620.193.4(043.2)
COBISS: 13908502 Povezava se bo odprla v novem oknu
Št. ogledov: 2884
Št. prenosov: 433
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Study of corrosion control of stainless steel "1.4057" with different inhibitors
Sekundarni povzetek: We have studied corrosion behaviour of stainless steel W. Nr. 14057 in a solution of H2SO4, with a concentration, c = 0,075 mol/L, with additions of various concentrations of inhibitors. We used four different inhibitors (Na3PO4, NaNO2, Na2O7Si3, Na2B4O7) and a combination of two ones (NaNO2/Na2B4O7). We performed experiments by the gravimetric method in accordance with ASTM G31 standards. We determine the loss of mass from which we calculate rate of corrosion and effectiveness of corrosion inhibitors. We also perform electrochemical measurements, using inhibitor NaNO2 with different concentrations. By analyzing the results, we found out that with increasing the adequate concentration of inhibitors, the corrosion process of the selected steel is reduced.
Sekundarne ključne besede: corrosion;stainless steel;inhibitors;gravimetric method;rate of corrosion;effectiveness of inhibitors;
URN: URN:SI:UM:
Vrsta dela (COBISS): Diplomsko delo
Komentar na gradivo: Univ. v Mariboru, Fak. za kemijo in kemijsko tehnologijo
Strani: XII, 49 f.
Ključne besede (UDK): applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;engineering;technology in general;inženirstvo;tehnologija na splošno;materials testing;commercial materials;power stations;economics of energy;preiskava materiala;blagoznanstvo;energetske centrale;energetika;
ID: 987267