diplomska naloga
Suzana Stokić (Avtor), Matjaž Kristl (Mentor), Mihael Drofenik (Komentor), Monika Inkret (Komentor)

Povzetek

Pri tem diplomskem delu smo površinsko obdelali nanodelce titanovega dioksida rutilne kristalne strukture s plaščem silicijevega in aluminijevega oksida. Za površinsko obdelavo nanodelcev TiO2 smo uporabili tri postopke. Princip oplaščenja nanodelcev je bila koprecipitacija, kjer smo z ustreznimi obarjalnimi reagenti dosegli nanos oksidnih plaščev na površino nanodelcev titanovega dioksida. Ugotovili smo, da so najbolje oplaščeni tisti nanodelci, ki so bili površinsko obdelani po postopku 3. Pri vseh treh postopkih je prihajalo do aglomeracije delcev, kar je otežilo oplaščevanje posameznih delcev. Dobljene vzorce smo karakterizirali s pomočjo rentgenske praškovne difrakcije (XRD), s transmisijskim elektronskim mikroskopom (TEM), z vrstičnim elektronskim mikroskopom (SEM), z rentgenskim fluorescenčnim spektrofotometrom (XRF) ter določili specifično površino delcev z BET metodo.

Ključne besede

nanodelci;titanov dioksid;površinska obdelava;oplaščenje;koprecipitacija;

Podatki

Jezik: Slovenski jezik
Leto izida:
Izvor: Maribor
Tipologija: 2.11 - Diplomsko delo
Organizacija: UM FKKT - Fakulteta za kemijo in kemijsko tehnologijo
Založnik: [S. Stokić]
UDK: 542.745(043.2)
COBISS: 14091030 Povezava se bo odprla v novem oknu
Št. ogledov: 3690
Št. prenosov: 394
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Surface coating of titanium dioxide nanoparticles with rutile crystal structure
Sekundarni povzetek: Nanoparticles of titanium dioxide with rutile crystal structure were coated with Al2O3 and SiO2. Three different processes were used for this surface treatment. Rutile nano TiO2 was coated by method of coprecipitation, where precipitating agents were added and aluminium and silicium oxide layers were formed on surface of nanoparticles. The results showed that the most optimal process was the third process. The samples were characterised by X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscope (SEM), X-ray fluorescence spectrometer (XRF) and SBET method.
Sekundarne ključne besede: nano TiO2;surface treatment;coating;coprecipitation;
URN: URN:SI:UM:
Vrsta dela (COBISS): Diplomsko delo
Komentar na gradivo: Univ. v Mariboru, Fak. za kemijo in kemijsko tehnologijo
Strani: VIII, 47 f.
Ključne besede (UDK): mathematics;natural sciences;naravoslovne vede;matematika;chemistry;crystallography;mineralogy;kemija;practical laboratory chemistry;preparative and experimental chemistry;praktična laboratorijska kemija;preparativna in eksperimentalna kemija;working with gases;
ID: 988680