diplomsko delo
Bojana Kušić (Avtor), Ivan Anžel (Mentor)

Povzetek

Zlitine z visoko vsebnostjo zlata se zaradi svojih specifičnih lastnosti čedalje več uporabljajo na različnih področjih industrije, in sicer v elektrotehniki in elektroniki, strojništvu, zlatarstvu, arhitekturi in v medicini, torej na področjih in v aplikacijah, kjer uporaba cenejših materialov ni mogoča. V tem diplomskem delu je analiziran problem spremljanja procesa rekristalizacije pri zlitini Au-0,5La z merjenjem mikrotrdote po Vickersu. Vzorci za študij rekristalizacije so bili hladno deformirani do stopnje deformacije med 82% in 84%. V odvisnosti od temperature smo z opazovanjem na optičnem mikroskopu zasledovali spreminjanje mikrostrukture in ugotovitve primerjali z vrednostmi izmerjenih mikrotrdot. Na podlagi primerjalne analize je bil spremljan potek procesa poprave in rekristalizacije. Rezultati in analiza so pokazali, da zaradi prisotnosti mreže intermetalne spojine metoda ugotavljanja temperature rekristalizacije z merjenjem mikrotrdote v odvisnosti od temperature rekristalizacijskega žarjenja ni primerna

Ključne besede

rekristalizacija zlitin;zlitine zlata;zlato;merjenje mikrotrdote;Au-0,5La;deformacije;mikrostruktura;

Podatki

Jezik: Slovenski jezik
Leto izida:
Izvor: Maribor
Tipologija: 2.11 - Diplomsko delo
Organizacija: UM FS - Fakulteta za strojništvo
Založnik: [B. Kušić]
UDK: 669.21.017-174(043.2)
COBISS: 15039254 Povezava se bo odprla v novem oknu
Št. ogledov: 2282
Št. prenosov: 187
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Recrystallization of Au-0,5 La alloy
Sekundarni povzetek: Alloys containing high percentage of pure gold are being used in various fields of industry like electronics, mechanical engineering, jewellery, architecture and medicine, where use of cheaper materials is not possible. This work analyses the problem of observing and evaluating the recrystallization process of Au-0,5la alloy by measuring microhardness by Vickers. All samples were cold deformed from 82 % to 84 % cold work and annealed at various temperatures after which their microhardness by Vickers was measured. Processes of the recovery and recrystallization were evaluated by comparing microhardness values in correlation with microstructure observation. Results and the analysis show that determining recrystallization temperature of the Au-0,5La alloy by measuring microhardness in correlation to microstructure observation is not appropriate due to presence of an intermetallic net Au6La.
Sekundarne ključne besede: recrystallization;gold based alloys;microhardness measurement;
URN: URN:SI:UM:
Vrsta dela (COBISS): Diplomsko delo
Komentar na gradivo: Univ. v Mariboru, Fak. za strojništvo
Strani: X, 57 f.
Ključne besede (UDK): applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;chemical technology;chemical and related industries;kemijska tehnologija;kemijske in sorodne industrije;metallurgy;metalurgija;nonferrous metals in general;neželezna metalurgija;neželezne kovine;
ID: 992289