Utrjanje betona z zakasnelo tvorbo etringita

doktorska disertacija

Samo Lubej (Avtor), Ivan Anžel (Mentor), Ladislav Kosec (Komentor)

Povzetek

Zakasnela tvorba etringita (Delayed Ettringite Formation - DEF) je kemična reakcija z dokazano škodljivim vplivom na hidratizirani beton. Kristali, ki pri tej kemicni reakciji nastanejo, lahko povzročijo nastanek razpok. Pozitivne spremembe prostornine, ki je posledica nastalih produktov prav tako poveča pritiske na stene razpok in poroznih mestih. Zaradi rasti kristalov etringita ima lahko mlad hidratizirani beton višje trdnosti, kar pa navadno pomeni spremljajoč pojav nastanek razpok in razpad betona. V disertaciji smo raziskali možnosti kako izkoristiti pozitivne volumensko spremembo, ki je posledica DEF za izboljšanje trdnostnih lastnosti drobno zrnatega betona. Ugotovili smo, da z dodajanjem aeranta in zelo kratkim časom vibriranja betona dosežemo takšno strukturo betona, kjer zračni mehurcki v hidratiziranem betonu predstavljajo nukleacijska mesta. Zakasnela tvorba etringita je z razpršenimi zračnimi mehurčki, ki so nastali od aeranta kontrolirana. Rast kristalov etringita ne povzroči hitrega povečanja trdnosti in razpada betona, temveč v fazi stabilizacije strukture doprinese 6% poveanje tlačne trdnosti ob minimalnem znižanju gostote hidratiziranega drobno zrnatega betona.

Ključne besede

zakasnela tvorba etringita;DEF;kontrolirana DEF;kristali etringita;aerirani beton;utrjanje;

Podatki

Jezik:	Slovenski jezik
Leto izida:	2011
Izvor:	Maribor
Tipologija:	2.08 - Doktorska disertacija
Organizacija:	UM FS - Fakulteta za strojništvo
Založnik:	[S. Lubej]
UDK:	691.332.5:666.972(043.3)
COBISS:	15902742
Št. ogledov:	2734
Št. prenosov:	139
Ocena:	0 (0 glasov)
Metapodatki:

Ostali podatki

Sekundarni jezik:	Angleški jezik
Sekundarni naslov:	Strength improvement with delayed ettringite formation
Sekundarni povzetek:	Delayed ettringite formation (DEF) is a chemical reaction with proven damaging effects on hydrated concrete. Ettringite crystals can cause cracks and their widening due to pressure on crack walls caused by the positive volume difference in the reaction. Concrete may show improvements in strength at early ages but further growth of cracks causes widening and spreading of these cracks through the concrete structure. In this study, a potential to utilise the positive volume difference in DEF in order to improve mechanical properties of hydrated fine grained concrete is investigated. Finely dispersed crystallization nuclei achieved by adding air-entraining agent (AEA) and short vibration of specimens is presented as the main prerequisite for such improvements. The study presents the method and mechanism for obtaining the required crystallisation nuclei. Controlling long-term DEF by providing AEA induced crystallisation nuclei prevented excessive and rapid initial strength improvements, and resulted in a 6% increase of compressive strength of fine grained concrete with only marginally lower density.
Sekundarne ključne besede:	delayed ettringite formation;DEF;controlled DEF;ettringite crystals;aerated concrete;strength improvement;Beton;Disertacije;
URN:	URN:SI:UM:
Vrsta dela (COBISS):	Doktorska disertacija
Komentar na gradivo:	Univ. v Mariboru, Fak. za gradbeništvo
Strani:	191 str.
Ključne besede (UDK):	applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;building (construction) trade;building materials;building practice and procedure;gradbeništvo;gradbeni materiali;gradbene obrti in dela;building materials;building components;gradiva;gradbeni [konstrukcijski] deli;applied sciences;medicine;technology;uporabne znanosti;medicina;tehnika;chemical technology;chemical and related industries;kemijska tehnologija;kemijske in sorodne industrije;glass industry;ceramics;cement and concrete;industrija stekla;keramika;cement in beton;gypsum;lime and cement industries;hard-setting materials;plasters and compositions;mortar and concrete;industrije mavca;apna in cementa;vezivni materiali;ometi in sestavne zmesi;malta in beton;
ID:	998198