Micromechanical analysis of constraint effect on fracture initiation in strength mis-matched welded joints
Miloš Dobrojević, Marko Rakin, Nenad Gubeljak, I. Cvijović, M. Zrilić, N. Krunich, Aleksandar Sedmak
Izvirni znanstveni članek
Oznake: lomna mehanika;duktilni lom;visokotrdnostna nizko legirana jekla;razpoke;nekovinski vključki;rast praznin;mikromehanski model;trdnostno neenaki zvarni spoji;fracture mechanics;ductile fracture;high strength low alloyed steel;cracks;micromechanical model;mismatched welded joints;constraint effect;void growth;
In this paper the micromechanical approach to ductile fracture was applied in a study of constraint effect crack growth initiation in mismatched welded joints. The single edged- notched bend specimens (precrack length ▫$a_o/W=0.32$▫) were experimentally and numerically analysed. The coupled micromec ...
Leto: 2007 Vir: Fakulteta za strojništvo (UM FS)
Ustava Republike Črne Gore
Svetlana Cvijović, Rudi Kocjančič
Diplomsko delo
Oznake: ustave;Črna Gora;diplomske naloge;
Ustava Republike Črne Gore
Leto: 2009 Vir: Fakulteta za upravo (UL FU)
The effect of compositional variations on the fracture toughness of 7000 Al-alloys
Maja Vratnica, Zorica Cvijović, Nenad Radović
Izvirni znanstveni članek
Oznake: aluminijeve zlitine;žilavost;mikrostruktura;kemijska sestava;
Leto: 2008 Vir: dLib.si Digitalna knjižnica Slovenije
The characterisation of Al-Si alloys in a thermally treated state
Darko Vuksanović, Momčilo Martinović, Petar Živković, Zorica Cvijović, Snežana Tripković
Izvirni znanstveni članek
Oznake: Al-Si alloys;Intermetallic phases;corrosion potential;polarisation resistance;corrosion current;
The characterisation! of Al-Si alloys in a thermally treated state
Leto: 2003 Vir: dLib.si Digitalna knjižnica Slovenije
An investigation of temperature-resistant aluminium alloys
Darko Vuksanović, Momčilo Martinović, Petar Živković, Zorica Cvijović, Snežana Tripković
Izvirni znanstveni članek
Oznake: Al-Si alloys;modified state;intermetallic phases;fracture morphology;
Leto: 2002 Vir: dLib.si Digitalna knjižnica Slovenije