Secondary title: | Comparison of HAZ fracture toughness measured by two types of small scale specimens |
Secondary abstract: | Samples of material with microstructures of four different HAZ situated at the fusion line were prepared on a Gleeble simulator. Specimens for the experimental determination of impact and fracture toughness were machined from samples. The fracture toughness was measured on two types of small pre-cracked specimens. The ▫$K_{Ic}$▫ was determined on round tensile specimens while the ▫$\theta_{c}$▫ was obtained from SENB specimens. The results obtained from the SENB specimens are too optimistic in comparison with the ▫$K_{Ic}$▫. The SENB specimens are not thick enough, even at very low fracture toughness. |
Secondary keywords: | weld joint;constructional steel;heat-affected zone (HAZ);fusion line;thermal influence;fracture toughness; |