zaključna naloga univerzitetnega študijskega programa I. stopnje Strojništvo
Uroš Margon (Avtor), Uroš Trdan (Mentor), Damjan Klobčar (Komentor)

Povzetek

V zaključni nalogi smo obravnavali mehanske lastnosti aluminijevih zlitin za gnetenje za uporabo v transportni industriji. Osredotočili smo se na trdnostne lastnosti, pridobljene po postopku varjenja s trenjem in mešanjem. V eksperimentalnem delu smo za zvarni spoj zlitine 2017A-T451 in 7075-T651, varjene pod različnimi pogoji, izvedli meritve hrapavosti in valovitosti ter izmerili mikrotrdoto v preseku zvarnega mesta. Nato smo poiskali povezave med izmerjenimi vrednostmi in varilnimi parametri. Izbrani vzorec smo pogledali pod mikroskopom ter opravili makro-in mikrostrukturno analizo. Najdene ekstremne vrednosti mikrotrdote smo na koncu primerjali s proučevanimi mikrostrukturnimi značilnostmi. Meritve hrapavosti so pokazale, da se nahaja največji aritmetični odstopek profila v smeri potovanja orodja, in sicer ob pogoju podajanja na obrat 25 vrt/cm pri vrednosti 5,4 [mikro]m. Najvišje vrednosti trdote so bile izmerjene pri vzorec s podajanjem na obrat 16 vrt/cm v zgornjem delu zvara v coni mešanja, in sicer pri okoli 170 HV0,2.

Ključne besede

diplomske naloge;mikrotrdota;visokotrdnostne aluminijeve zlitine;varjenje s trenjem in mešanjem;topografija;mikrostruktura;makrostruktura;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.11 - Diplomsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [U. Margon ]
UDK: 539.4.01+620.179.2(043.2)
COBISS: 16235035 Povezava se bo odprla v novem oknu
Št. ogledov: 1845
Št. prenosov: 323
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Microhardness in Dissimilar High-Strength Aluminium Alloy Welds
Sekundarni povzetek: In this study we investigated the mechanical properties of wrought aluminium alloys for transportation industry use. We focused on the strength properties, obtained by the friction stir welding process. In the experimental part, we took measurements of surface roughness and waveviness of friction stir welded joints in 2017A-4 and 7075-T6 aluminium alloys that were welded using different welding parameters. We also measured the microhardness profile through the transverse cross-section of butt joints. After finding the correlation between measured values and the welding process parameters, macroscopic and microscopic analyses for the chosen specimen were performed. Then we investigate the possible correlation between measured microhardness extremes and microstructure properties. The topography analysis showed us that the highest value of mean roughness (5,4 [micro]m) was observed in the direction parallel to the welding direction in the area where welding process at a feed per revolution of 25 rev/cm took place. The maxima of microhardness were observed at the upper layer of the welding sample that was welded at a feed per revolution of 16 rev/cm with a value of 170 HV0,2. In the lower layer of the same specimen, the minimum of 96 HV0,2 was measured.
Sekundarne ključne besede: microhardness;high-strength aluminium alloys;friction stir welding;topography;microstructure;macrostructure;
Vrsta dela (COBISS): Zaključna naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. v Ljubljani, Fak. za strojništvo
Strani: XIV, 41 f.
ID: 10959936
Priporočena dela:
, zaključna naloga univerzitetnega študijskega programa I. stopnje Strojništvo
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo
, zaključna naloga univerzitetnega študijskega programa I. stopnje Strojništvo
, zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
, diplomsko delo Visokošolskega strokovnega študijskega programa I. stopnje Strojništvo