zaključna naloga Univerzitetnega študijskega programa I. stopnje Strojništvo - Razvojno raziskovalni program
Povzetek
Poleg stalne zahteve zmanjšanja emisij ter prevoznih stroškov na račun teže tovora, so lahki materiali z dobrimi mehanskimi lastnostmi vedno bolj uporabljeni v industriji. Visoko-trdnostne aluminijeve zlitine so ene izmed njih, vendar pa jih je s konvencionalnimi talilnimi postopki varjenja nemogoče uspešno spajati, še posebno v primeru spajanja raznorodnih zlitin. Iz tega vidika je postopek varjenja s trenjem in gnetenjem (FSW) izredno perspektiven saj omogoča kakovosten zvarni spoj brez napak tudi v primeru spajanja teh materialov. V zaključnem delu smo iz FSW spoja izdelanega iz raznorodnih aluminijevih zlitin serij 2017A-T451 in 7075-T651 izrezali vzorce ter jih ustrezno pripravili za nadaljnje meritve in analize. Nato smo izvedli podrobne meritve mikrotrdote v vzdolžni smeri zvara v več linijah. Hkrati smo iz vidika preučitve vpliva orodja ter vnosa toplote opravili meritve na različnih globinah pod površjem temena zvarnega spoja. Nato smo vzorce makroskopsko pregledali ter izvedli mikroskopske meritve prehodnih območij zvarnega spoja ter mesta kjer so bili izmerjeni ekstremi mikrotrdot. Profile mikrotrdot smo nato poskušali ustrezno povezati z mikrostrukturnimi značilnostmi FSW spoja.
Ključne besede
diplomske naloge;raznorodne visoko-trdnostne aluminijeve zlitine;varjenje z gnetenjem;makrostruktura;mikrotrdota;mikrostruktura;
Podatki
Jezik: |
Slovenski jezik |
Leto izida: |
2021 |
Tipologija: |
2.11 - Diplomsko delo |
Organizacija: |
UL FS - Fakulteta za strojništvo |
Založnik: |
[N. Avbelj] |
UDK: |
669.715:621.791:620.17(043.2) |
COBISS: |
76954371
|
Št. ogledov: |
686 |
Št. prenosov: |
91 |
Ocena: |
0 (0 glasov) |
Metapodatki: |
|
Ostali podatki
Sekundarni jezik: |
Angleški jezik |
Sekundarni naslov: |
Analisys of dissimilar aluminium alloy FSW in longitudinal direction |
Sekundarni povzetek: |
In addition to the constant demand to reduce emissions and transport costs at the expense of cargo weight, lightweight materials with good mechanical properties are increasingly used in industry. High-strength aluminium alloys are one of them, but it is impossible to successfully join them with conventional fusion welding processes, especially in the case of joining dissimilar alloys. From this point of view, the process of friction stir welding (FSW) is extremely promising as it enables a quality welded joint without defects even in the case of joining these materials. In the final part, we cut samples from FSW joint made of dissimilar aluminum alloys of the 2017A-T451 and 7075-T651 series and prepared them accordingly for further measurements and analyzes. We then performed detailed microhardness measurements in the longitudinal direction of the weld in several lines. At the same time, from the point of view of studying the influence of the tool and heat input, we performed measurements at different depths below the top surface of the welded joint. Then we macroscopically examined the samples and made microscopic measurements of the transition areas of the welded joint and places where the microhardness extremes were measured. Then we attempted to appropriately relate the microhardness profiles to the microstructural characteristics of the FSW joint. |
Sekundarne ključne besede: |
thesis;dissimilar high-strength aluminium alloys;friction stir welding;microhardness;macrostructures; |
Vrsta dela (COBISS): |
Zaključna naloga |
Študijski program: |
0 |
Komentar na gradivo: |
Univ. v Ljubljani, Fak. za strojništvo |
Strani: |
XV, 37 f. |
ID: |
13411358 |