magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
Sani Veljanovski (Avtor), Damjan Klobčar (Mentor)

Povzetek

Cilj dela je bil določiti vpliv procesnih parametrov pri oblikovnem obločnem navarjanju (WAAM) na zaostale napetosti. Z žico iz konstrukcijskega jekla G3Si1 premera 1,2 mm smo navarjali preproste geometrije na osnovni material. Teoretični del zajema opis procesa izdelave WAAM ter mehanizmov nastanka in merjenja zaostalih napetosti. Predstavljen je plan načrtovanja eksperimentov za izdelavo vzorcev s postopkom WAAM ter plan merjenja napetosti z metodo XRD. Rezultate smo analizirali glede na procesne parametre izdelave: jakost varilnega toka, medvarkovno temperaturo in strategijo izdelave. Jakost varilnega toka ima največji vpliv na zaostale napetosti. Strategija navarjanja ima velik vpliv na obliko navarka, saj se lahko zgodi, da nam z napačno strategijo navarjanja ne bo uspeli izdelati izdelka. Najmanjši vpliv na zaostale napetosti ima medvarkovna temperatura. Glede na rezultate eksperimentov priporočamo izmenično strategijo navarjanja s čim manjšim vnosom energije.

Ključne besede

magistrske naloge;oblikovno obločno navarjanje (WAAM);dodajalne tehnologije;navarjanje;zaostale napetosti;rentgenska odbojna metoda;

Podatki

Jezik: Slovenski jezik
Leto izida:
Tipologija: 2.09 - Magistrsko delo
Organizacija: UL FS - Fakulteta za strojništvo
Založnik: [S. Veljanovski]
UDK: 621.791.75:669.14:620.1(043.2)
COBISS: 28819203 Povezava se bo odprla v novem oknu
Št. ogledov: 394
Št. prenosov: 97
Ocena: 0 (0 glasov)
Metapodatki: JSON JSON-RDF JSON-LD TURTLE N-TRIPLES XML RDFA MICRODATA DC-XML DC-RDF RDF

Ostali podatki

Sekundarni jezik: Angleški jezik
Sekundarni naslov: Residual stress in WAAM welding of G3Si1 structural steel
Sekundarni povzetek: Master thesis focuses on influence of process parameters in the WAAM manufacturing on residual stress. We welded simple geometry to the base material % structural steel. Samples were manufactured by a MAG welding process using G3Si1 welding wire of 1.2 mm diameter. The theoretical part includes a description of the WAAM manufacturing process and measurement of residual stress. A plan of experiment for production of samples using WAAM and measuring residual stress using X-ray diffraction is presented. The results were analyzed on terms of process parameters: welding current, manufacturing strategy and welding temperature. Welding current has the highest influence on residual stress. The manufacturing strategy has a great influence on the shape of the weld. It can happen that with wrong strategy we will not be able to make a desired product. The smallest effect on residual stress has welding temperature. Based on experiments we recommend alternating strategy with lowest possible welding current.
Sekundarne ključne besede: master thesis;Wire + Arc Additive Manufacturing (WAAM);additive manufacturing;welding;residual stress;X-Ray diffraction;
Vrsta dela (COBISS): Magistrsko delo/naloga
Študijski program: 0
Konec prepovedi (OpenAIRE): 1970-01-01
Komentar na gradivo: Univ. Ljubljana, Fak. za strojništvo
Strani: XXII, 56 str., [2] f. pril.
ID: 12003902
Priporočena dela:
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, zaključna naloga Projektno aplikativnega programa I. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo
, magistrsko delo magistrskega študijskega programa II. stopnje Strojništvo